ELECTROLESS NICKEL PLATING - A REVIEW.

被引：0
|
作者：
Spencer, Lester F.
机构：
来源：
Metal Finishing | 1975年 / 73卷 / 01期
关键词：
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Since electroless nickel can be heat treated to high hardness values, it will provide good abrasion and wear resistance, provided that lubrication is used and the surface temperature remains below 600 degree F. High internal tensile stresses cause peeling, cracking and reduced fatigue life. A compressive stress will improve adhesion. Corrosion resistance of platings to various reagents are shown in chart form.
引用
收藏
页码：38 / 44
相关论文
共 50 条
  • [1] ELECTROLESS NICKEL - A REVIEW.
    Brown, L.D.
    Finishing, 1982, 6 (08): : 15 - 16
  • [2] Electroless Nickel Plating – A Review
    C. A. Loto
    Silicon, 2016, 8 : 177 - 186
  • [3] Electroless Nickel Plating - A Review
    Loto, C. A.
    SILICON, 2016, 8 (02) : 177 - 186
  • [4] Nickel electroless plating: a review
    Ben Amor, Y.
    Frateur, I.
    Mat, P.
    Boualam, M.
    MATERIAUX & TECHNIQUES, 2014, 102 (01):
  • [5] ELECTROLESS NICKEL DEPOSITION - A REVIEW.
    Hsieh, Stephen A.K.
    Chung, M.F.
    Product Finishing (London), 1981, 34 (11): : 20 - 46
  • [6] ELECTROLESS NICKEL PLATING ON SILICON
    IWASA, H
    YOKOZAWA, M
    TERAMOTO, I
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1968, 115 (05) : 485 - &
  • [7] CHEMICAL (ELECTROLESS) NICKEL PLATING
    ALBERTH, W
    GALVANOTECHNIK, 1979, 70 (06): : 502 - 505
  • [8] Electroless nickel plating of diamond
    Tong, Kui
    Xu, Enxia
    Xin, Rongsheng
    Pan, Yuehong
    Cailiao Baohu/Materials Protection, 2000, 33 (02): : 19 - 20
  • [9] ELECTROLESS NICKEL PLATING ON TITANIUM
    GRAHAM, GH
    PLATING AND SURFACE FINISHING, 1983, 70 (11): : 46 - 46
  • [10] Electroless nickel plating of magnesium
    Fairweather, WA
    TRANSACTIONS OF THE INSTITUTE OF METAL FINISHING, 1997, 75 : 113 - 117
12345