Elongational behavior of epoxy during curing

被引：0
|
作者：
Takiguchi, Osamu [1 ]
Sugimoto, Masataka [1 ]
Taniguchi, Takashi [1 ]
Koyama, Kiyohito [1 ]
机构：
[1] Graduate School of Science and Engineering, Yamagata University, Yonezawa 992-8510, Japan
来源：
Journal of Applied Polymer Science | 2009年 / 114卷 / 02期
关键词：
Elongational behavior of epoxy (epoxy/cur-ing agent 100/0.5; w/w) cured at various conditions over the critical gelation time was investigated. Dynamic viscoelastic measurements of the epoxy system were performed and the critical gelation time of epoxy was determined according to the frequency dependence of G' and G proposed by Winter and Chambon. Elongational behavior of epoxy cured for various times were measured. Epoxy; cured over the critical gelation time; showed strain hardening and elongational behavior similar to a crosslinked rubber. Increase of elongational viscosity of the sample occurred early; and the sample broke at small strain as curing time increased. The effect of strain rate on the elonga-tional stress of epoxy cured near the critical gelation time was measured at various strain rates. For epoxy cured for critical gelation time only; high stress at a small strain rate was represented as strain rate increased. When increasing curing time further; the tensile stress converged on a single curve regardless of strain rate; and samples broke at nearly the same stress and strain. © 2009 Wiley Periodicals; Inc;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Journal article (JA)
引用
收藏
页码：1018 / 1024
相关论文
共 50 条
  • [1] Elongational Behavior of Epoxy During Curing
    Takiguchi, Osamu
    Sugimoto, Masataka
    Taniguchi, Takashi
    Koyama, Kiyohito
    JOURNAL OF APPLIED POLYMER SCIENCE, 2009, 114 (02) : 1018 - 1024
  • [2] RHEOLOGICAL BEHAVIOR OF EPOXY ACRYLATE PREPOLYMER DURING UV CURING
    OTSUBO, Y
    AMARI, T
    WATANABE, K
    JOURNAL OF APPLIED POLYMER SCIENCE, 1984, 29 (12) : 4071 - 4080
  • [3] Curing behavior of epoxy asphalt
    Jianying Yu
    Peiliang Cong
    Shaopeng Wu
    Songbo Cheng
    Journal of Wuhan University of Technology-Mater. Sci. Ed., 2009, 24 : 462 - 465
  • [4] Curing Behavior of Epoxy Asphalt
    余剑英
    Journal of Wuhan University of Technology(Materials Science), 2009, 24 (03) : 462 - 465
  • [5] Curing behavior of epoxy asphalt
    Yu Jianying
    Cong Peiliang
    Wu Shaopeng
    Cheng Songbo
    JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2009, 24 (03): : 462 - 465
  • [6] Curing Behavior of Epoxy Asphalt
    余剑英
    Journal of Wuhan University of Technology(Materials Science Edition), 2009, 24 (03) : 462 - 465
  • [7] Modeling of Viscoelastic Behavior of an Epoxy Molding Compound During and After Curing
    Lin, Yeong-Jyh
    Hwang, Sheng-Jye
    Lee, Huei-Huang
    Huang, Durn-Yuan
    IEEE TRANSACTIONS ON COMPONENTS PACKAGING AND MANUFACTURING TECHNOLOGY, 2011, 1 (11): : 1755 - 1760
  • [8] MODELING THE DIELECTRIC BEHAVIOR OF EPOXY-RESIN BLENDS DURING CURING
    MAISTROS, GM
    BUCKNALL, CB
    POLYMER ENGINEERING AND SCIENCE, 1994, 34 (20): : 1517 - 1528
  • [9] Characterization of the curing behavior of epoxy resins
    Rodríguez Agudo J.A.
    Völker-Pop L.
    Giehl C.
    Puntigam X.
    Adhaesion Kleben und Dichten, 2024, 68 (1-2): : 30 - 33
  • [10] Curing Behavior for Microencapsulated Curing Agents on Epoxy Resin Systems
    Zhang, Lulu
    Wang, Xi
    PROCEEDINGS OF THE 5TH INTERNATIONAL CONFERENCE ON CIVIL ENGINEERING AND TRANSPORTATION 2015, 2016, 30 : 1739 - 1742
12345