Super-long life Fatigue properties of Al-Si-Cu die Casting Alloy by using ultrasonic fatigue tests

被引：0

作者：

Yamada, Koji ^{[1
]}

Miyakawa, Susumu ^{[1
]}

机构：

[1] Material Engineering R and Dept., Denso Corporation, 1-1 Showa-cho, Kariya shi, Aichi, 448-8661, Japan

来源：

Nihon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A | 2006年 / 72卷 / 05期

关键词：

Aluminum alloys - Die casting - Fatigue of materials - Fatigue testing - Mathematical models - Stress intensity factors;

D O I：

10.1299/kikaia.72.749

中图分类号：

学科分类号：

摘要：

Super long life Fatigue properties of Al-Si-Cu Die Casting Alloy were investigated by using ultrasonic fatigue tests at room temperature. The results were compared to fatigue data acquired from conventional fatigue tests, and the fatigue strength were stsudied quantitatively considering the casting defect that was the origin of fatigue crack. The main results obtained are as follows : (1) The S-N curves obtained by using ultrasonic fatigue tests broke in the regime around 10' cycles-as well as conventional fatigue tests. (2) The origin of fatigue crack is casting defect and the fracture surface at around the fatigue crack initiation portion was Mode I fracture surface as well as conventional fatigue tests. (3) From the S-N curve, the fracture mode and etc., ultrasonic fatigue tests seem to be the effective evaluation method of super-long life fatigue properties. (4) Below σ = 100MPa, some specimen were broke, some were not broke. The √area parameter model with casting defect size can explain whether a specimen breaks, but the fatigue limit predicted by the √area parameter model shows the upper level (5) The fatigue limit predicted by the relationship between the stress intensity factor range ΔKCD obtained from the casting defect size in the regime more than 107 cycles and casting defect size √area are in good agreement with the fatigue limit from the S-N curve.

引用

页码：749 / 756

共 50 条

[1] Super-long life fatigue properties of aluminum alloy die-casting related with internal or surface defects
Material Eng. R and D Dept., DENSO Corporation, 1-1 Showa-cho, Kariya-shi, Aichi, 448-8661, Japan
[J]. Nihon Kikai Gakkai Ronbunshu A, 2006, 11 (1751-1758):
[2] Fatigue properties and microstructure of Al-Si-Cu system casting alloys
Kobayashi, T
Ito, T
Yao, Q
Fatahalla, N
[J]. MATERIALS SCIENCE AND TECHNOLOGY, 1999, 15 (09) : 1037 - 1043
[3] Effect of microstructure on fatigue crack propagation characteristic of Al-Si-Cu die casting alloys
Graduate School of Toyohashi, University of Technology, I-1. Tempaku-cho, Toyohashi-shi, Aichi 441-8580
不详
不详
[J]. Keikinzoku J Jpn Inst Light Met, 9 (443-449):
[4] The fatigue damage development in a cast Al-Si-Cu alloy
Dietrich, Lech
Radziejewska, Joanna
[J]. MATERIALS & DESIGN, 2011, 32 (01) : 322 - 329
[5] Fatigue of an Al-Si gravity die casting alloy
Styles, C.M.
Reed, P.A.S.
[J]. Materials Science Forum, 2000, 331
[6] Fatigue of an Al-Si gravity die casting alloy
Styles, CM
Reed, PAS
[J]. ALUMINIUM ALLOYS: THEIR PHYSICAL AND MECHANICAL PROPERTIES, PTS 1-3, 2000, 331-3 : 1457 - 1462
[7] Tensile properties of Al-Si-Cu die-casting alloy in the partial solidification state
[J]. 2013, Springer-Verlag (63):
[8] Interfacial Heat Transfer during Die Casting of an Al-Si-Cu Alloy
Hamasaiid, A.
Wang, G.
Davidson, C.
Dour, G.
Dargusch, M. S.
[J]. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2009, 40A (13): : 3056 - 3058
[9] Interfacial Heat Transfer during Die Casting of an Al-Si-Cu Alloy
A. Hamasaiid
G. Wang
C. Davidson
G. Dour
M.S. Dargusch
[J]. Metallurgical and Materials Transactions A, 2009, 40 : 3056 - 3058
[10] Elevated temperature low cycle fatigue of a gravity casting Al-Si-Cu alloy used for engine cylinder heads
Fan, K. L.
Liu, X. S.
He, G. Q.
Chen, H.
[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2015, 632 : 127 - 136

← 1 2 3 4 5 →