Characteristics of LiMO2 (M = Co, Ni, Ni0.2Co0.8, Ni0.8Co0.2) powders prepared from solution of their acetates

被引：0
|
作者：
Arof, A.K. [1 ]
机构：
[1] Physics Department, University of Malaya, 50603 Kuala Lumpur, Malaysia
来源：
Journal of Alloys and Compounds | 2008年 / 449卷 / 1-2期
关键词：
Stoichiometric quantities of the acetates of lithium; cobalt and nickel were dissolved in distilled water and stirred with a magnetic stirrer. After complete dissolution was obtained; the solutions were heated at 120 °C under continuous stirring until some dark colored powder materials were formed. These precursor materials were divided into three batches and heated at 250 °C (for 24 h); 370 °C (for 24 h) and 800 °C for 10 h. The precursor and calcined samples were X-rayed. The X-ray diffractograms for the prepared samples were compared to that of commercialized samples and those published in the literature. The Bragg peak with Miller indices (0 0 3) in the diffractogram of the LiNi0.8Co0.2O2 prepared sample showed a lower intensity compared to the (1 0 4) peak. The ratio of the (0 0 3) to (1 0 4) peaks for the LiNi0.2Co0.8O2 sample is 1.56. Lattice parameters showed that the LiCoO2 and LiNi0.2Co0.8O2 samples produced by the method in the present investigation have potential to exhibit good electrochemical performance when used as electrodes in lithium ion batteries. © 2007 Elsevier B.V. All rights reserved;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Journal article (JA)
引用
收藏
页码：288 / 291
相关论文
共 50 条
  • [1] Characteristics of LiMO2 (M = Co, Ni, Ni0.2Co0.8, Ni0.8Co0.2) powders prepared from solution of their acetates
    Arof, A. K.
    [J]. JOURNAL OF ALLOYS AND COMPOUNDS, 2008, 449 (1-2) : 288 - 291
  • [2] Improvement of transport properties of Lix(Ni0.8Co0.2)O2 oxide in the formation of Lix(Ni0.8Co0.2)O2/PANI composite
    Mosqueda, Y
    Pérez-Cappe, E
    Rodríguez, G
    Varela, JA
    Souza, E
    [J]. Physica Status Solidi C - Conference and Critical Reviews, Vol 2, No 10, 2005, 2 (10): : 3774 - 3777
  • [3] Preparation of LiNi0.8Co0.2O2 cathode material for lithium secondary batteries from spherical α-Ni0.8Co0.2(OH)2
    Ying, JR
    Wan, CR
    Jiang, CY
    [J]. JOURNAL OF INORGANIC MATERIALS, 2001, 16 (05) : 821 - 826
  • [4] 以球形α-Ni0.8Co0.2(OH)2制备锂离子电池正极材料LiNi0.8Co0.2O2
    应皆荣
    万春荣
    姜长印
    [J]. 无机材料学报, 2001, (05) : 821 - 826
  • [5] 电解Co0.2Ni0.8合金制备LiCo0.2Ni0.8O2的研究
    魏进平
    夏小勇
    阎杰
    宋德瑛
    潘桂玲
    [J]. 电池, 2002, (S1) : 53 - 55
  • [6] Synthesis and electrochemical properties of Li[Ni0.8Co0.1Mn0.1]O2 and Li[Ni0.8Co0.2]O2 via co-precipitation
    Kim, Myung-Hyoon
    Shin, Ho-Suk
    Shin, Dongwook
    Sun, Yang-Kook
    [J]. JOURNAL OF POWER SOURCES, 2006, 159 (02) : 1328 - 1333
  • [7] Novel Ho(Ni0.8Co0.2)3 nanoflakes produced by high energy ball - milling
    Bajorek, Anna
    Berger, Clement
    Prusik, Krystian
    Wojtyniak, Marcin
    Chelkowska, Grayna
    [J]. MATERIALS CHARACTERIZATION, 2017, 128 : 43 - 53
  • [8] The effects of sintering time on the structure and electrochemical properties of Li(Ni0.8Co0.2)O2
    Gover, R
    Kanno, R
    Mitchell, B
    Hirano, A
    Kawamoto, Y
    [J]. JOURNAL OF POWER SOURCES, 2000, 90 (01) : 82 - 88
  • [9] Microstructure and electrochemical properties of melt-spun Nd0.8Mg0.2(Ni0.8Co0.2)3.8 hydrogen storage alloy
    潘崇超
    蔡吴鹏
    王震
    耿朝青
    于荣海
    [J]. Journal of Rare Earths, 2010, 28 (01) : 100 - 103
  • [10] Preparation of high density Ni0.8Co0.2 (OH)2 used as precursor for cathode of lithium battery
    College of Chemistry and Environmental Science, Henan Normal University, Xinxiang 453007, China
    [J]. Gongneng Cailiao, 2007, 10 (1717-1719): : 1717 - 1719
12345