Microstructure and hot corrosion behaviors of a γ-toughened Cr13Ni5Si2/Cr3Ni5Si2 ternary metal silicide alloy

被引：0
|
作者：
Yuan, L. [1 ]
Wang, H.M. [1 ]
机构：
[1] Laboratory of Laser Materials Processing and Manufacturing, School of Materials Science and Engineering, Beihang University (formerly Beijing University of Aeronautics and Astronautics), 37 Xueyuan Road, Beijing, 100191, China
来源：
Journal of Alloys and Compounds | 2009年 / 479卷 / 1-2期
关键词：
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Journal article (JA)
引用
收藏
页码：217 / 224
相关论文
共 50 条
  • [1] Microstructure and hot corrosion behaviors of a γ-toughened Cr13Ni5Si2/Cr3Ni5Si2 ternary metal silicide alloy
    Yuan, L.
    Wang, H. M.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2009, 479 (1-2) : 217 - 224
  • [2] Corrosion behaviors of a γ-toughened Cr13Ni5Si2/Cr3Ni5Si2 multi-phase ternary metal silicide alloy in NaCl solution
    Yuan, L.
    Wang, H. M.
    ELECTROCHIMICA ACTA, 2008, 54 (02) : 421 - 429
  • [3] A wear resistant ductile metal-toughened Cr13Ni5Si2 ternary metal silicide alloy
    Fang, YL
    Tang, HB
    Wang, HM
    INTERMETALLICS, 2006, 14 (07) : 750 - 758
  • [4] Microstructure and dry sliding wear resistance of a Cr13Ni5Si2 ternary metal silicide alloy
    Tang, HB
    Fang, YL
    Wang, HM
    ACTA MATERIALIA, 2004, 52 (07) : 1773 - 1783
  • [5] High-temperature sliding wear resistance of a ductile metal-toughened Cr13Ni5Si2 ternary metal silicide alloy
    Fang, Y. L.
    Wang, H. M.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2007, 433 (1-2) : 114 - 119
  • [6] CORROSION BEHAVIORS OF Ni BASE SOLID SOLUTION-TOUGHENED Cr13Ni5Si2 ALLOY IN Cl- CONTAINING SOLUTIONS
    Yuan Lei
    Wang Huaming
    ACTA METALLURGICA SINICA, 2009, 45 (11) : 1384 - 1389
  • [7] Corrosion properties of a Cr13Ni5Si2-based metal silicide alloy
    Yuan, L.
    Wang, H. M.
    INTERMETALLICS, 2008, 16 (09) : 1149 - 1155
  • [8] High-temperature sliding wear resistant Cr13Ni5Si2/γ-Ni ternary metal silicide composite
    Fang, Yanli
    Li, An
    Zhang, Lingyun
    Wang, Huaming
    Fuhe Cailiao Xuebao/Acta Materiae Compositae Sinica, 2006, 23 (06): : 80 - 85
  • [9] Microstructure and high-temperature sliding wear resistance of a Cr3Si/Cr13Ni5Si2 intermetallic alloy
    Zhang, LQ
    Wang, HM
    RARE METAL MATERIALS AND ENGINEERING, 2004, 33 (05) : 512 - 514
  • [10] High-temperature sliding wear resistance of a Cr3Si/Cr13Ni5Si2 multiphase intermetallic alloy
    Zhang, LQ
    Wang, HM
    MATERIALS LETTERS, 2003, 57 (18) : 2710 - 2715
12345