Effect of surface plasma W-Mo alloying on microstructure and wear resistance of powder metallurgy gears

被引：0
|
作者：
Wei D.-B. [1 ,2 ]
Li M.-F. [1 ,2 ]
Liu X.-Q. [1 ,2 ]
Liu Z.-L. [1 ,2 ]
Zou Y.-W. [2 ,3 ]
Huang X.-X. [2 ,3 ]
Zou D.-H. [2 ,3 ]
机构：
[1] School of Material Science and Technology, Nanjing University of Aeronautics and Astronautics, Nanjing
[2] Jiangsu Automotive Powder Metallurgy Engineering Technology Research Center, Changshu
[3] Changshu Hua-de Powder Metallurgy Co., Ltd, Changshu
来源：
Surface Technology | 2021年 / 50卷 / 01期
基金：
中国博士后科学基金;
关键词：
Double glow plasma surface metallurgy; Gear; Microhardness; Microstructure; Tribological properties; W-Mo alloy coating;
D O I：
10.16490/j.cnki.issn.1001-3660.2021.01.026
中图分类号：
学科分类号：
摘要：
The work aims to improve the hardness and wear resistance of powder metallurgy gear through surface plasma W-Mo alloying. The W-Mo alloy coating was prepared on the surface of powder metallurgy gear by double glow plasma surface metallurgy technology. The surface morphology and chemical composition of the W-Mo alloy coating was characterized by scanning electron microscope (SEM) and energy dispersive X-ray spectroscope (EDS). The microhardness of the substrate and W-Mo alloy coating was measured by Vickers microhardness tester. The effect of plasma W-Mo alloying on the abrasion resistance of powder metallurgical gears was studied by reciprocating friction and wear experiments under different loads. The W-Mo alloy coating was successfully prepared on the surface of powder metallurgy gear by double glow plasma metallurgy technology. The alloy coating was metallurgically bonded with the substrate. The average microhardness of substrate increased from 145.8HV0.1 to 344.4HV0.1 after double glow plasma surface W-Mo alloying, an increase of about 2.4 times. The friction and wear tests under different loads indicated that the friction coefficient declined from 0.6~0.7 to about 0.45~0.5 after W-Mo alloying, a decrease of about 30%. With the increasing of the load, the wear volume of the substrate and the W-Mo alloy coating increased. The specific wear rate decreased from 18.70×10−5~36.16×10−5 mm3/(N·m) of the powder metallurgy gear to 2.99× 10−5~8.79×10−5 mm3/(N·m) of the W-Mo alloy coating, which was a decrease of about 74%~84%. The wear mechanism of the substrate consisted of adhesive wear and abrasive wear, while wear mechanism of the W-Mo alloy coating was slight abrasive wear. The W-Mo alloy coating improves the hardness and wear resistance of powder metallurgy gear significantly. The surface plasma W-Mo alloying technology provides a new technical method for the surface strengthening of powder metallurgy gear. © 2021, Chongqing Wujiu Periodicals Press. All rights reserved.
引用
收藏
页码：305 / 312
页数：7
相关论文
共 19 条
  • [1] Feng S.C., Wang Y.H., Ding R.F., Application and prospect of powder metallurgy in steel enterprises[J], Powder Metallurgy Technology, 33, 4, pp. 296-300, (2015)
  • [2] Moravcikova-Gouvea L., Moravcik I., Omasta M., Et al., High-strength Al<sub>0.2</sub>Co<sub>1.5</sub>CrFeNi<sub>1.5</sub>Ti high-entropy alloy produced by powder metallurgy and casting: A comparison of microstructures, mechanical and tribological properties[J], Materials Characterization, 159, (2020)
  • [3] Ou X., Zhao S.X., Application of powder metallurgy parts in the field of transmission[J], Metallurgy and Materials, 39, 5, pp. 101-103, (2019)
  • [4] Whittaker D., Powder metallurgy for gear production: Current status and potential future trends[J], Materials & Design, 12, 2, pp. 97-100, (1991)
  • [5] Kianian B., Comparing acquisition and operation life cycle costs of powder metallurgy and conventional wrought steel gear manufacturing techniques[J], Procedia CIRP, 81, pp. 1101-1106, (2019)
  • [6] Wei H.W., Analysis of gear failure in coal mine machinery and countermeasures[J], Shanxi Coking Coal Science & Technology, 35, 4, pp. 50-53, (2011)
  • [7] Ren B.L., Miao Q., Liang W.P., Et al., Effect of surface carburizing temperature on wear resistance of Ti<sub>2</sub>AlNb alloy[J], Transactions of Materials and Heat Treatment, 37, 9, pp. 151-156, (2016)
  • [8] Zhang L., Wei D.B., Zhang P.Z., Et al., Effect of W-Mo alloying of double glow plasma on γ-TiAl surface on oxidation behavior[J], Surface Technology, 47, 4, pp. 17-23, (2018)
  • [9] Jiang J., Hu J., Yang X., Et al., Microstructure and annealing behavior of Cr-coatings deposited by double glow plasma on AISI 5140 steel[J], Results in Physics, 15, (2019)
  • [10] Wang H.F., Tang B., Li X.Y., Microstructure and wear resistance of N-doped TiO<sub>2</sub> coatings grown on stainless steel by plasma surface alloying technology[J], Journal of Iron and Steel Research International, 18, 7, pp. 73-78, (2011)
12