Fatigue analysis of crack growing rate and stress intensity factor for stress corrosion cracking in a pipeline system

被引：0
|
作者：
Shahani, A.R. [1 ]
Mahdavi, E. [1 ]
Amidpour, M. [1 ]
机构：
[1] Department of Mechanical Engineering, K. N. Toosi University of Technology, Tehran, Iran
来源：
World Academy of Science, Engineering and Technology | 2009年 / 33卷
关键词：
Brittle fracture - Stress corrosion cracking - Offshore structures - Fatigue crack propagation - Hydrogen embrittlement - Pipelines - Corrosion fatigue - Pipeline corrosion - Hydrogen;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
引用
收藏
页码：785 / 788
相关论文
共 50 条
  • [1] Crack Growth Rate Analysis of Stress Corrosion Cracking
    Alkateb, Mohamed
    Tadic, Srdan
    Sedmak, Aleksandar
    Ivanovic, Ivana
    Markovic, Svetislav
    TEHNICKI VJESNIK-TECHNICAL GAZETTE, 2021, 28 (01): : 240 - 247
  • [2] Threshold stress intensity factor and crack growth rate for stress corrosion cracking of simulated heat affected zone in caustic solution
    Pal, Sarvesh
    Ibrahim, R. N.
    Raman, R. K. Singh
    ENGINEERING FRACTURE MECHANICS, 2011, 78 (01) : 13 - 26
  • [3] INITIATION OF STRESS-CORROSION CRACKING AND FATIGUE CRACK UNDER COMPRESSIVE STRESS
    CHU, WY
    HSIAO, CM
    LIU, TH
    YAO, J
    ENGINEERING FRACTURE MECHANICS, 1984, 20 (02) : 271 - 279
  • [4] Analysis of the Stress Intensity Factor of a Pipeline Surface with a Pit-Crack
    Yu J.
    Li X.
    Tan Y.
    Jin C.
    Feng Z.
    Han X.
    Fu F.
    Tianjin Daxue Xuebao (Ziran Kexue yu Gongcheng Jishu Ban)/Journal of Tianjin University Science and Technology, 2019, 52 (05): : 522 - 528
  • [5] Experimental research on residual stress and stress intensity factor for fatigue crack
    Liu, Zhi
    Wang, Ruigang
    Fu, Chengsong
    Jixie Gongcheng Xuebao/Chinese Journal of Mechanical Engineering, 1995, 31 (05): : 97 - 102
  • [6] Stress Corrosion Cracking of Pipeline Steels
    Bingyan FANG
    Journal of Materials Science & Technology, 2002, (01) : 3 - 6
  • [7] Stress corrosion cracking of pipeline steels
    Fang, BY
    Han, EH
    Zhu, ZY
    Wang, JQ
    Ke, W
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2002, 18 (01) : 3 - 6
  • [8] Stress corrosion cracking of pipeline steels
    Fang, Bingyan
    Han, Enhou
    Zhu, Ziyong
    Wang, Jianqiu
    Ke, Wei
    Journal of Materials Science and Technology, 2002, 18 (01): : 3 - 6
  • [9] Stress Corrosion Cracking in Pipeline Steels
    Plumtree, A.
    Lambert, S. B.
    ADVANCES IN FRACTURE AND DAMAGE MECHANICS XII, 2014, 577-578 : 5 - 8
  • [10] COMPARISON BETWEEN THRESHOLD STRESS AND CRACK INITIATION STRESS INTENSITY FOR SULFIDE STRESS-CORROSION CRACKING
    WILDE, BE
    DOYLE, MJ
    CORROSION, 1979, 35 (06) : 273 - 276
12345