Characterization of the AWS 317l weld overlay applied by twin wire GMAW on ASTM A516 Gr 60 steel used in oil and gas industry

被引：0

作者：

da Silva M.M. ^{[1
]}

Oliveira W.C. ^{[1
]}

Maciel T.M. ^{[1
]}

dos Santos M.A. ^{[1
]}

Motta M.F. ^{[2
]}

机构：

[1] Universidade Federal de Campina Grande, Departamento de Engenharia Mecânica, Laboratório de Soldagem, Paraíba, Campina Grande

[2] Universidade Federal do Ceará, Departamento de Engenharia Mecânica

来源：

Soldagem e Inspecao | 2010年 / 15卷 / 03期

关键词：

AISI; 317l; Partially diluted zones; Twin wire GMAW; Weld overlay;

D O I：

10.1590/s0104-92242010000300009

中图分类号：

学科分类号：

摘要：

The aim of this study was to evaluate the metallurgical characteristics of weld overlay applied by Twin Wire GMAW process nd the AWS E317L filler metal on ASTM A 516 Gr 60 base metal. During welding it was employed two levels of heat input (H = 1170kJ/m and H = 1530kJ/m) and a mixture of argon and oxygen (95% Ar and 5% O2) as shielding gas. Besides, all welds were carried ut without preheat, however, an interpass temperature of 150°C was used. Then, the specimens were characterized using optical icroscopy and microhardness tests. The results showed an increase in dilution and heat affect zone extension when the heat input ncreases. Moreover, there was also the formation of partially diluted zones (PDZ) along the fusion line, presenting values above 300HV. The formation of PDZ was larger for the highest heat input level.

引用

页码：225 / 233

页数：8

共 3 条

[1] Characterization of the AWS 317L Weld Overlay Applied by Twin Wire GMAW on ASTM A516 Gr 60 Steel Used in Oil and Gas Industry
da Silva, Marcos Mesquita
Oliveira, Wellington Cordeiro
Maciel, Theophilo Moura
dos Santos, Marco Antonio
Motta, Marcelo Ferreira
SOLDAGEM & INSPECAO, 2010, 15 (03): : 225 - 233
[2] AWS ERNiCrMo-3 filler metal weld overlay in ASTM A516 Gr.60 behavior thus aging thermal treatment
De Magalhães, Sitonio Gomes
Motta, Marcelo Ferreira
De Miranda, Hélio Cordeiro
Farias, Jesualdo Pereira
Soldagem e Inspecao, 2008, 13 (04): : 265 - 275
[3] AWS ERNiCrMo-3 filler metal weld overlay in ASTM A516 Gr.60 behavior thus aging thermal treatment
de Magalhaes, Sitonio Gomes
Motta, Marcelo Ferreira
de Miranda, Helio Cordeiro
Farias, Jesualdo Pereira
SOLDAGEM & INSPECAO, 2008, 13 (04): : 266 - 276

← 1 →