Fabrication of carbon nanotube reinforced Al composites with well-balanced strength and ductility

被引：0
|
作者：
机构：
[1] [2,Yang, Xudong
[2] Liu, Enzuo
[3] Shi, Chunsheng
[4] He, Chunnian
[5] Li, Jiajun
[6] 1,Zhao, Naiqin
[7] Kondoh, Katsuyoshi
来源：
Zhao, N. (nqzhao@tju.edu.cn) | 1600年 / Elsevier Ltd卷 / 563期
关键词：
An approach was developed to fabricate carbon nanotube (CNT)-reinforced Al composites. In a typical process; the Co catalyst was evenly deposited on the surface of Al powder by impregnation route; and then the CNTs were grown in the Al powder by chemical vapor deposition to obtain CNT/Al powders. After ball-milling of the obtained powders for a short time; the CNT/Al composites were fabricated by compacting; sintering and hot extrusion of the ball-milled powders. During this process; the well dispersed CNT reinforcement is deeply embedded in the Al powder forming an effective interface bonding with matrix. As a result; the CNT/Al composites containing 2.5 wt.% CNTs exhibit the ultimate tensile strength of 334 MPa which is 1.7 times higher than that of unreinforced Al; and good ductility of ∼18% elongation to failure. Thus; well-balanced strength and ductility are achieved in CNT-reinforced Al composites.© 2013 Elsevier B.V. All rights reserved;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Journal article (JA)
引用
收藏
相关论文
共 50 条
  • [1] Fabrication of carbon nanotube reinforced Al composites with well-balanced strength and ductility
    Yang, Xudong
    Liu, Enzuo
    Shi, Chunsheng
    He, Chunnian
    Li, Jiajun
    Zhao, Naiqin
    Kondoh, Katsuyoshi
    JOURNAL OF ALLOYS AND COMPOUNDS, 2013, 563 : 216 - 220
  • [2] A novel (AlN + Si3N4)/Al composite with well-balanced strength and ductility
    Xu, Qingfei
    Ma, Xia
    Hu, Kaiqi
    Gao, Tong
    Liu, Xiangfa
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2018, 726 : 113 - 119
  • [3] Lightweight Al3Ti-based medium-entropy alloys with well-balanced strength and ductility
    Diao, Guijiang
    He, Anqiang
    Wu, Mingyu
    Tang, Yunqing
    Chen, W. G.
    Li, Q. Y.
    Li, Dongyang
    SCRIPTA MATERIALIA, 2024, 242
  • [4] Achieving well-balanced strength and ductility in GNFs/Ti composite via laminated architecture design
    Mu, X. N.
    Zhang, H. M.
    Chen, P. W.
    Cheng, X. W.
    Yang, L.
    Chang, S.
    Duan, H. Q.
    Liu, L.
    CARBON, 2022, 189 : 173 - 185
  • [5] Strength versus ductility in carbon nanotube reinforced nickel matrix nanocomposites
    Borkar, Tushar
    Hwang, Jaewon
    Hwang, Jun Yeon
    Scharf, Thomas W.
    Tiley, Jaimie
    Hong, Soon Hyung
    Banerjee, Rajarshi
    JOURNAL OF MATERIALS RESEARCH, 2014, 29 (06) : 761 - 769
  • [6] Strength versus ductility in carbon nanotube reinforced nickel matrix nanocomposites
    Tushar Borkar
    Jaewon Hwang
    Jun Yeon Hwang
    Thomas W. Scharf
    Jaimie Tiley
    Soon Hyung Hong
    Rajarshi Banerjee
    Journal of Materials Research, 2014, 29 : 761 - 769
  • [7] Fabrication of well-dispersed, multiwall carbon nanotube-reinforced aluminum matrix composites
    Javadi, A. H.
    Mirdamadi, Sh
    Faghihisani, M. A.
    Shakhesi, S.
    Soltani, R.
    NEW CARBON MATERIALS, 2012, 27 (03) : 161 - 165
  • [8] Structure optimization for improving the strength and ductility of heterogeneous carbon nanotube/Al-Cu-Mg composites
    Ma, K.
    Liu, Z. Y.
    Liu, K.
    Chen, X. Grant
    Xiao, B. L.
    Ma, Z. Y.
    CARBON, 2021, 178 : 190 - 201
  • [9] An Improved Approach to Manufacture Carbon Nanotube Reinforced Magnesium AZ91 Composites with Increased Strength and Ductility
    Nasiri, Samaneh
    Yang, Guang
    Spiecker, Erdmann
    Li, Qianqian
    METALS, 2022, 12 (05)
  • [10] Optimizing matrix and fiber/matrix interface to achieve combination of strength, ductility and toughness in carbon nanotube-reinforced carbon/carbon composites
    Feng, Lei
    Li, Kezhi
    Xue, Bei
    Fu, Qiangang
    Zhang, Leilei
    MATERIALS & DESIGN, 2017, 113 : 9 - 16
12345