Comparative study on hydrogen induced cracking sensitivity of two commercial API 5L X80 steels

被引：0
|
作者：
Xing, Yunying [1 ]
Yang, Zhile [1 ]
Yao, Xingcheng [1 ]
Wang, Xiuyun [1 ]
Lu, Minxu [1 ]
Zhang, Lei [1 ]
Qiao, Lijie [1 ]
机构：
[1] Institute for Advanced Materials and Technology, University of Science and Technology Beijing, Beijing,100083, China
来源：
International Journal of Pressure Vessels and Piping | 2022年 / 196卷
关键词：
D O I：
暂无
中图分类号：
学科分类号：
摘要：
引用
收藏
相关论文
共 50 条
  • [1] Comparative study on hydrogen induced cracking sensitivity of two commercial API 5L X80 steels
    Xing, Yunying
    Yang, Zhile
    Yao, Xingcheng
    Wang, Xiuyun
    Lu, Minxu
    Zhang, Lei
    Qiao, Lijie
    INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING, 2022, 196
  • [2] Hydrogen embrittlement of API 5L X60 and API 5L X80 steels
    Araújo B.A.
    Palma J.A.
    Vilar E.O.
    Silva A.A.
    Informacion Tecnologica, 2011, 22 (06): : 129 - 140
  • [3] Experimental Characterization of Hydrogen Embrittlement in API 5L X60 and API 5L X80 Steels
    Araujo, Bruno Allison
    Travassos, Gabriel Dias
    Silva, Antonio Almeida
    Vilar, Eudesio Oliveira
    Carrasco, Jorge Palma
    Araujo, Carlos Jose
    ADVANCED COMPUTATIONAL ENGINEERING AND EXPERIMENTING, 2011, 478 : 34 - 39
  • [4] A Comparative Investigation of the Corrosion Resistance and HIC Suceptibility of API 5L X65 and API 5L X80 Steels
    Quispe-Aviles, Janeth Marlene
    Hincapie-Ladino, Duberney
    Falleiros, Neusa Alonso
    de Melo, Hercilio Gomes
    MATERIALS RESEARCH-IBERO-AMERICAN JOURNAL OF MATERIALS, 2019, 22 (01):
  • [5] A comparative study of hydrogen induced cracking behavior in API 5L X60 and X70 pipeline steels
    Mohtadi-Bonab, M. A.
    Szpunar, J. A.
    Razavi-Tousi, S. S.
    ENGINEERING FAILURE ANALYSIS, 2013, 33 : 163 - 175
  • [6] STUDY OF THE SUSCEPTIBILITY OF API 5L X80 GIRTH WELDS TO SULFIDE STRESS CORROSION CRACKING AND HYDROGEN EMBRITTLEMENT
    Ballesteros, Adriana Forero
    da Cunha Ponciano, Jose A.
    Bott, Ivani de S.
    PROCEEDINGS OF THE ASME INTERNATIONAL PIPELINE CONFERENCE 2010, VOL 1, 2010, : 375 - 380
  • [7] A Comparative Study of Hydrogen-Induced Cracking Resistances of API 5L B and X52MS Carbon Steels
    Figueredo, Rodrigo Monzon
    de Oliveira, Mariana Cristina
    de Paula, Leandro Jesus
    Acciari, Heloisa Andrea
    Codaro, Eduardo Norberto
    INTERNATIONAL JOURNAL OF CORROSION, 2018, 2018
  • [8] Microstructural Evaluation of API 5L X80 Pipeline Steels Submitted to Different Cooling Rates
    Bott, I. S.
    Vieira, A. A. H.
    de Souza, L. F. G.
    Rios, P. R.
    THERMEC 2009, PTS 1-4, 2010, 638-642 : 3146 - +
  • [9] Residual Stress Study of API 5L X80 Steel Welded Joints
    Araujo, Bruno Allison
    Silva Sousa Lima, Maria do Socorro
    Maciel, Theophilo Moura
    Silva, Antonio Almeida
    Soares, Emanuel Pereira
    SOLDAGEM & INSPECAO, 2013, 18 (03): : 217 - 226
  • [10] Evaluation of the diffusivity and susceptibility to hydrogen embrittlement of API 5L X80 steel welded joints
    Araujo, B. A.
    Maciel, T. M.
    Palma Carrasco, J.
    Vilar, E. O.
    Almeida Silva, A.
    INTERNATIONAL JOURNAL OF MULTIPHYSICS, 2013, 7 (03) : 183 - 195
12345