Magnetic properties of M -doped (M=Mn, Cr, or V) ZnSi N2

被引：0
|
作者：
Rufinus, Jeff [1 ]
机构：
[1] Science Division, Widener University, Chester, PA 19013, United States
来源：
Journal of Applied Physics | 2009年 / 105卷 / 07期
关键词：
The current interest in the emerging field of semiconductor spintronics is mostly focused on transition-metal-doped binary materials; e.g; Mn-doped GaAs; GaN; etc; Recently; however; the explorations of transition-metal-doped ternary semiconductors have intensified due to some experimental confirmations of high Curie temperature in chalcopyrite compounds. In ternary materials; there are possibilities of having ferromagnetic or antiferromagnetic configurations; depending on which metal site was substituted by the dopant. A density functional theory within generalized gradient approximation study was performed on M -doped (M=Mn; Cr; or V) ternary material ZnSi N2. The objective of this study is to determine whether substitutional transition metal in a group II (Zn) site and in a group IV (Si) site will be ferromagnetic or antiferromagnetic. The results show both Mn- and Cr-doped ZnSi N2 to be antiferromagnetic if (Mn; Cr) substitute Zn site and ferromagnetic if (Mn; Cr) substitute Si site. On the other hand; V-doped ZnSi N2 was found to be ferromagnetic; independent of the substitution sites. © 2009 American Institute of Physics;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Journal article (JA)
引用
收藏
相关论文
共 50 条
  • [1] Magnetic properties of M-doped, (M=Mn, Cr, or V) ZnSiN2
    Rufinus, Jeff
    JOURNAL OF APPLIED PHYSICS, 2009, 105 (07)
  • [2] Magnetic properties of M-doped (M = Ti, V, or Cr) GaN clusters
    Rufinus, J.
    JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2007, 310 (02) : 1666 - 1668
  • [3] Magnetic behaviour of doped dimer compounds Sr3Cr2-xMxO8 (M = V, Mn)
    Chattopadhyay, S.
    Giri, S.
    Majumdar, S.
    EUROPEAN PHYSICAL JOURNAL B, 2012, 85 (01):
  • [4] EFFECT OF ADDED ELEMENTS M(M=V, CR, MN, CO, NI) ON SOFT MAGNETIC-PROPERTIES OF FE-ZR-N FILMS
    NAKANISHI, K
    SHIMIZU, O
    YOSHIDA, S
    IEEE TRANSACTIONS ON MAGNETICS, 1991, 27 (06) : 5322 - 5324
  • [5] Magnetic Properties of Transition-Metal-Doped Tubular Gold Clusters: M@Au24 (M = V, Cr, Mn, Fe, Co, and Ni)
    Yang, Aping
    Fa, Wei
    Dong, Jinming
    JOURNAL OF PHYSICAL CHEMISTRY A, 2010, 114 (12): : 4031 - 4035
  • [6] 2D Magnetic MXenes (M11-xM2x)3C2 (M1 = V, Cr; M2 = Mn, Cr): The Stability, Ordering, and Magnetic Properties
    Zamkova, Natalia G.
    Zhandun, Vyacheslav S.
    Inorganic Chemistry, 2024, 63 (51) : 24295 - 24305
  • [7] Magnetic properties of Mn-doped chalcopyrites:: (BeSn,BeGe,MgGe)N2
    Rufinus, Jeff
    DeWinter, Jennifer L.
    JOURNAL OF APPLIED PHYSICS, 2008, 103 (07)
  • [8] Magnetic behaviour of doped dimer compounds Sr3Cr2−xMxO8 (M = V, Mn)
    S. Chattopadhyay
    S. Giri
    S. Majumdar
    The European Physical Journal B, 2012, 85
  • [9] Mechanical Properties and Electronic Structures of M (M=Ti, V, Cr, Mn and Fe) Doped β-Si3N4 from First-Principle
    Long, Min
    Huang, Fuxiang
    Xu, Liangyu
    Li, Xuemei
    Yang, Zhou
    Leng, Yue
    Mei, Shini
    JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2024, 39 (03): : 639 - 644
  • [10] Mechanical Properties and Electronic Structures of M (M=Ti, V, Cr, Mn and Fe) Doped β-Si3N4 from First-Principle
    龙敏
    黄福祥
    XU Liangyu
    LI Xuemei
    YANG Zhou
    LENG Yue
    MEI Shini
    Journal of Wuhan University of Technology(Materials Science), 2024, 39 (03) : 639 - 644
12345