Structure evolution and thermal stability of SMAT-derived nanograined layer on Ti-25Nb-3Mo-3Zr-2Sn alloy at elevated temperatures

被引：0
|
作者：
机构：
[1] Huang, Run
[2] Han, Yong
来源：
Han, Y. (yonghan@mail.xjtu.edu.cn) | 1600年 / Elsevier Ltd卷 / 554期
关键词：
A nanocrystalline layer; which consists of pure β phase with average grain size of about 30 nm on Ti-25Nb-3Mo-3Zr-2Sn alloy; was fabricated by surface mechanical attrition treatment (SMAT). The microstructure evolution; phase transitions and thermal stability of the nanocrystalline layer during isochronal annealing at temperatures of 300-600 °C were investigated by XRD and TEM. During annealing; the nanocrystalline layer underwent recovery; recrystallization and significant grain growth. Recovery occurs at temperatures from 300 to 400 °C resulting in strain relaxation; dislocation annihilation and a very limited growth of β grains dominated by re-ordering of grain boundaries (GBs). α Precipitates start to precipitate along the β GBs at 350 °C; which exhibit equiaxed morphology with size less than 10 nm. Recrystallization proceeds at a higher temperature up to 450 °C leading to a reduction of β grain size. Due to the pinning effect of the α precipitates; β grains sizes can be maintained less than 100 nm until the annealing temperature increased to 550 °C; e.g; 0.41 Tm (melting temperature in K); above which significant grain growth occurs to overstep nanocystalline scale; and the growth activation energy of β grains is calculated as 40.8 kJ/mol. The abnormal low value is caused by the nonequilibrium GBs of β grains in the as-SMATed surface layer; which increase atomic mobility even in the presence of pinning effect of the α precipitates on the β GBs. © 2012 Elsevier B.V. All rights reserved;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Journal article (JA)
引用
收藏
相关论文
共 50 条
  • [1] Structure evolution and thermal stability of SMAT-derived nanograined layer on Ti-25Nb-3Mo-3Zr-2Sn alloy at elevated temperatures
    Huang, Run
    Han, Yong
    JOURNAL OF ALLOYS AND COMPOUNDS, 2013, 554 : 1 - 11
  • [2] Thermal analysis of precipitation reactions in a Ti-25Nb-3Mo-3Zr-2Sn alloy
    Kent, Damon
    Pas, Steven
    Zhu, Suming
    Wang, Gui
    Dargusch, Matthew S.
    APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING, 2012, 107 (04): : 835 - 841
  • [3] The effect of SMAT-induced grain refinement and dislocations on the corrosion behavior of Ti-25Nb-3Mo-3Zr-2Sn alloy
    Huang, Run
    Han, Yong
    MATERIALS SCIENCE & ENGINEERING C-MATERIALS FOR BIOLOGICAL APPLICATIONS, 2013, 33 (04): : 2353 - 2359
  • [4] Tribocorrosion behaviour of a biomedical Ti-25Nb-3Mo-3Zr-2Sn alloy in Ringer's solution
    Wang, Zhenguo
    Huang, Weijiu
    Li, Yan
    He, Haoran
    Zhou, Yongtao
    Zheng, Ziqing
    MATERIALS SCIENCE AND ENGINEERING C-MATERIALS FOR BIOLOGICAL APPLICATIONS, 2017, 76 : 1094 - 1102
  • [5] Role of grain size in the regulation of osteoblast response to Ti-25Nb-3Mo-3Zr-2Sn alloy
    Huang, Run
    Lu, Shemin
    Han, Yong
    COLLOIDS AND SURFACES B-BIOINTERFACES, 2013, 111 : 232 - 241
  • [6] Processing considerations for cast Ti-25Nb-3Mo-3Zr-2Sn biomedical alloys
    Bermingham, M. J.
    McDonald, S. D.
    Buddery, A. J.
    StJohn, D. H.
    Dargusch, M. S.
    MATERIALS SCIENCE & ENGINEERING C-MATERIALS FOR BIOLOGICAL APPLICATIONS, 2011, 31 (07): : 1520 - 1525
  • [7] Electrochemical behaviour of Ti-25Nb-3Mo-3Zr-2Sn biomedical alloy in different simulated physiological environments
    Wang, Z.
    Huang, W.
    Meng, X.
    MATERIALS SCIENCE AND TECHNOLOGY, 2015, 31 (11) : 1335 - 1341
  • [8] An investigation of the mechanical behaviour of fine tubes fabricated from a Ti-25Nb-3Mo-3Zr-2Sn alloy
    Zhang, Yaowu
    Kent, Damon
    Wang, Gui
    St John, David
    Dargusch, Matthew
    MATERIALS & DESIGN, 2015, 85 : 256 - 265
  • [9] Strengthening of cast Ti-25Nb-3Mo-3Zr-2Sn alloy through precipitation of α in two discrete crystallographic orientations
    Paladugu, Mohanchand
    Kent, Damon
    Wang, Gui
    Yu, Zhentao
    Dargusch, Matthew S.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2010, 527 (24-25): : 6601 - 6606
  • [10] Micro-abrasion-corrosion behaviour of a biomedical Ti-25Nb-3Mo-3Zr-2Sn alloy in simulated physiological fluid
    Wang, Zhenguo
    Li, Yan
    Huang, Weijiu
    Chen, Xiaoli
    He, Haoran
    JOURNAL OF THE MECHANICAL BEHAVIOR OF BIOMEDICAL MATERIALS, 2016, 63 : 361 - 374
12345