Corrosion Resistance of Passivation Films on Four Typical Hot-dip Galvanized Plates

被引：0
|
作者：
Min L. [1 ,4 ]
Rong S. [1 ,4 ]
Changcheng W. [2 ,4 ]
Min G. [3 ]
Baoyong W. [2 ]
Chen Z. [2 ]
Nini D. [2 ]
Yangze L. [2 ]
Yongzhuang L. [1 ]
机构：
[1] Research Institute of Technology of Shougang Group Co., Ltd., Beijing
[2] Shougang Jingtang United Iron and Steel Co., Ltd., Hebei
[3] Marketing Center, Beijing Shougang Shares Co., Ltd, Beijing
[4] Corrosion Resistance of Passivation Films on Four Typical Hot-dip Galvanized Plates[J], Surface Technology
来源：
Surface Technology | 2024年 / 53卷 / 06期
关键词：
Corrosion resistance;
D O I：
10.16490/j.cnki.issn.1001-3660.2024.06.009
中图分类号：
学科分类号：
摘要：
The work aims to analyze the composition of four passivation films for hot-dip galvanized plates, and investigate the corrosion resistance and corrosion protection mechanism of different passivation films. The microstructure and chemical composition of four passivation films were analyzed by SEM, XPS, GDS, IR and wetting angle. The corrosion resistance of the © 2024 Chongqing Wujiu Periodicals Press. All rights reserved.
引用
收藏
页码：99 / 110
页数：11
相关论文
共 28 条
  • [1] DEFLORIAN F, ROSSI S, FEDEL M, Et al., Electrochemical Investigation of High-Performance Silane Sol–Gel Films Containing Clay Nanoparticles, Progress in Organic Coatings, 69, 2, pp. 158-166, (2010)
  • [2] FEDEL M, OLIVIER M, POELMAN M, Et al., Corrosion Protection Properties of Silane Pre-Treated Powder Coated Galvanized Steel, Progress in Organic Coatings, 66, 2, pp. 118-128, (2009)
  • [3] KONG G, LU J T, ZHANG S H, Et al., A Comparative Study of Molybdate/Silane Composite Films on Galvanized Steel with Different Treatment Processes, Surface and Coatings Technology, 205, 2, pp. 545-550, (2010)
  • [4] KOLTSOV A, CORNU M J, LOISON D., Characterization by Different Analytical Techniques of SiO<sub>2</sub> and Silane Thin Films Deposited on Rough Hot-Dip Galvanized Steel Surfaces, Surface and Coatings Technology, 206, 11, pp. 2759-2768, (2012)
  • [5] ZHU D Q, VAN OOIJ W J., Enhanced Corrosion Resistance of AA 2024-T3 and Hot-Dip Galvanized Steel Using a Mixture of Bis-[Triethoxysilylpropyl]Tetrasulfide and Bis-[Trimethoxysilylpropyl]Amine, Electrochimica Acta, 49, 7, pp. 1113-1125, (2004)
  • [6] FEDEL M, DRUART M E, OLIVIER M, Et al., Compatibility between Cataphoretic Electro-Coating and Silane Surface Layer for the Corrosion Protection of Galvanized Steel, Progress in Organic Coatings, 69, 2, pp. 118-125, (2010)
  • [7] OLIVIER M G, FEDEL M, SCIAMANNA V, Et al., Study of the Effect of Nanoclay Incorporation on the Rheological Properties and Corrosion Protection by a Silane Layer, Progress in Organic Coatings, 72, 1, pp. 15-20, (2011)
  • [8] ZANDI-ZAND R, ERSHAD-LANGROUDI A, RAHIMI A., Silica Based Organic–Inorganic Hybrid Nanocomposite Coatings for Corrosion Protection, Progress in Organic Coatings, 53, 4, pp. 286-291, (2005)
  • [9] XIAO W, MAN R L, MIAO C, Et al., Study on Corrosion Resistance of the BTESPT Silane Cooperating with Rare Earth Cerium on the Surface of Aluminum-Tube, Journal of Rare Earths, 28, 1, pp. 117-122, (2010)
  • [10] METROKE T L, KACHURINA O, KNOBBE E T., Spectroscopic and Corrosion Resistance Characterization of Amine and Super Acid-Cured Hybrid Organic–Inorganic Thin Films on 2024-T3 Aluminum Alloy, Progress in Organic Coatings, 44, 3, pp. 185-199, (2002)
123