Study on thermal fatigue fracture characteristics of a cast steel for wheel

被引：0
|
作者：
He, Qingfu [1 ]
Song, Zhikun [1 ]
机构：
[1] Northern Jiaotong Univ., Beijing 100044, China
来源：
Kang T'ieh/Iron and Steel (Peking) | 2002年 / 37卷 / 12期
关键词：
Cast steel - Cycling temperature - Etching pits - Thermal fatigue damage;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
引用
收藏
页码：50 / 52
相关论文
共 50 条
  • [1] Experimental study on mode II crack fracture and fatigue of wheel steel
    Xing, LX
    Zhang, YZ
    Lin, JZ
    FATIGUE '99: PROCEEDINGS OF THE SEVENTH INTERNATIONAL FATIGUE CONGRESS, VOLS 1-4, 1999, : 2621 - 2626
  • [2] A study on the rolling contact fatigue mechanism of ZC-L cast wheel steel
    Zhang, Guanzhen
    Liu, Chunpeng
    Wu, Si
    Cong, Tao
    Wu, Yi
    Zhang, Bin
    Ren, Ruiming
    ENGINEERING FAILURE ANALYSIS, 2023, 148
  • [3] Study on characteristic of thermal fatigue cracking damage of wheel casting steel
    Tiedao Xuebao, 5 (109-111):
  • [4] Probe into thermal fatigue damage behavior of wheel cast steel at 450 °C [similar to] 20 °C
    School of Mechanical and Electronic Control Engineering, Beijing Jiaotong University, Beijing 100044, China
    Beijing Jiaotong Daxue Xuebao, 2007, 1 (8-10):
  • [5] FATIGUE STRENGTH CHARACTERISTICS OF CAST STEEL WELD JOINTS
    Kim, Ho Jung
    Kim, Seong Min
    Lee, Jae Myung
    Kim, Myung Hyun
    OMAE2011: PROCEEDINGS OF THE ASME 30TH INTERNATIONAL CONFERENCE ON OCEAN, OFFSHORE AND ARCTIC ENGINEERING, VOL 3: MATERIALS TECHNOLOGY, 2011, : 523 - 530
  • [6] Fatigue Reliability Curves for China Railway Grade B Cast Steel Wheel
    Liang, H. Q.
    Zhao, Y. X.
    Li, Y.
    MATERIALS ENGINEERING FOR ADVANCED TECHNOLOGIES, PTS 1 AND 2, 2011, 480-481 : 352 - +
  • [7] Random Fatigue Limits of China Railway Grade B Cast Steel Wheel
    Zhao, Y. X.
    Yang, B.
    Wang, Z. G.
    MATERIALS ENGINEERING FOR ADVANCED TECHNOLOGIES, PTS 1 AND 2, 2011, 480-481 : 347 - +
  • [8] Thermal fatigue and fracture mechanics analysis of grey cast iron
    Guo, Chengbi
    Zhou, Weisheng
    Jinshu Xuebao/Acta Metallurgica Sinica, 1988, 24 (06):
  • [9] THERMAL FATIGUE AND FRACTURE MECHANICS ANALYSIS OF GREY CAST IRON
    GUO Chengbi ZHOU Weisheng Dalian Institute of Technology
    Acta Metallurgica Sinica(English Letters), 1989, (03) : 194 - 200
  • [10] Overload Fracture of Cast Aluminum Wheel
    Weishaupt, E. R.
    Stevenson, M. E.
    Sprague, J. K.
    JOURNAL OF FAILURE ANALYSIS AND PREVENTION, 2014, 14 (06) : 702 - 706
12345