Flow-accelerated corrosion in gas compression piping

被引：0
|
作者：
CMRDI, Cairo, Egypt [1 ]
机构：
来源：
Mater Perform | / 2卷 / 46-50期
关键词：
D O I：
暂无
中图分类号：
学科分类号：
摘要：
A gas compression system consisting of two modules experienced one defective injection point on the first module, where wall thinning occurred at the 12 o'clock position close to the injection site. A piping section from the failed module, including the injection point and spool, was subjected to failure analysis to determine whether the failure was related to material selection or operating conditions of the system.
引用
收藏
相关论文
共 50 条
  • [1] Flow-Accelerated Corrosion in Gas Compression Piping
    El-Sayed, Mohamed Hanafy
    [J]. MATERIALS PERFORMANCE, 2015, 54 (02) : 46 - 50
  • [2] Estimation of Flow-Accelerated Corrosion Rate in Nuclear Piping System
    Hazra, Indranil
    Pandey, Mahesh D.
    Jyrkama, Mikko, I
    [J]. JOURNAL OF NUCLEAR ENGINEERING AND RADIATION SCIENCE, 2020, 6 (01):
  • [3] The COMSY - Code for the Detecting of Piping Degradation Due to Flow-Accelerated Corrosion
    Zander, Andre
    Nopper, Helmut
    [J]. PROCEEDINGS OF THE ASME PRESSURE VESSELS AND PIPING CONFERENCE - 2008, VOL 6, PT A AND B, 2009, : 905 - 910
  • [4] Disturbed flow and flow-accelerated corrosion in oil and gas production
    Efird, KD
    [J]. JOURNAL OF ENERGY RESOURCES TECHNOLOGY-TRANSACTIONS OF THE ASME, 1998, 120 (01): : 72 - 77
  • [5] Beware of Flow-Accelerated Corrosion
    Buecker, Brad
    [J]. CHEMICAL ENGINEERING, 2013, 120 (03) : 38 - 40
  • [6] Flow-accelerated corrosion & cavitation
    Jonas, Otakar
    [J]. Water and Wastes Digest, 2009, 49 (01): : 22 - 24
  • [7] The NPP Leibstadt Program for the Prevention of Piping Degradation due to Flow-Accelerated Corrosion Phenomena
    Zander, Andre
    Janning, Carsten
    [J]. PROCEEDINGS OF THE ASME PRESSURE VESSELS AND PIPING CONFERENCE, VOL 6, PTS A AND B, 2010, : 903 - 908
  • [8] PROBABILISTIC ESTIMATION OF FLOW-ACCELERATED CORROSION RATE AT THE WELDED JOINTS OF THE NUCLEAR PIPING SYSTEM
    Lu, Dongliang
    Pandey, M. D.
    Jyrkama, M. I.
    [J]. PROCEEDINGS OF THE ASME PRESSURE VESSELS AND PIPING CONFERENCE, PVP 2012, VOL 2, 2012, : 311 - 317
  • [9] MODELLING MATERIAL EFFECTS IN FLOW-ACCELERATED CORROSION
    Phromwong, P.
    Lister, Derek
    Uchida, S.
    [J]. 15TH INTERNATIONAL CONFERENCE ON ENVIRONMENTAL DEGRADATION OF MATERIALS IN NUCLEAR POWER SYSTEMS-WATER REACTORS, 2011, : 925 - 937
  • [10] Flow-accelerated corrosion: A critical issue revisited
    Buecker, Brad
    [J]. POWER ENGINEERING, 2007, 111 (07) : 20 - +
12345