Influence of ambient-temperature corrosion on the oxidation behavior of Al-Si coatings

被引：0
|
作者：
Zhang, Qi [1 ]
Song, Fu-Bin [1 ]
Wang, Hua-Ge [2 ]
Luo, Jun-Hua [1 ]
机构：
[1] Sch. of Materials Sci. and Eng., Beijing Univ. Aero. and Astronautics, Beijing 100083, China
[2] SAERDI, Shenyang 110015, China
来源：
Chinese Journal of Aeronautics | 2002年 / 15卷 / 04期
关键词：
Alumina - Corrosion - Oxidation resistance - Superalloys;
D O I：
10.1016/S1000-9361(11)60160-X
中图分类号：
学科分类号：
摘要：
The high-temperature oxidation behavior of Al-Si coatings on the Ni-base superalloy DZ125, with and without the ambient-temperature corrosion test, was investigated. The results show that the isothermal oxidation behavior of the corroded coating changes, which has the higher mass gain than that of the original coating during the initial oxidation stage. Moreover, the cyclic oxidation resistance of the corroded coating decreases severely. The oxide scale was primarily composed of Al2O3, contaminated with TiO2 that was due to the increase of Ti content after the room-temperature corrosion test.
引用
收藏
页码：244 / 249
相关论文
共 50 条
  • [1] Effect of pre-oxidation and sea salt on the hot corrosion behavior of MCrAlY coatings and Al-Si coatings
    Yang, Zhiqiang
    Zhang, Jun
    Luo, Chaoyong
    Yu, Chuan
    Li, Mei
    Han, Wei
    SURFACE & COATINGS TECHNOLOGY, 2024, 477
  • [2] The Influence of Microstructure of Al-Si Alloy and Microarc Oxidation Modes on Corrosion Resistance of the Formed Coatings
    Dudareva, Natalia Y.
    Zaynullina, Liliya I.
    Ustimova, Elena I.
    MATERIALS TODAY-PROCEEDINGS, 2019, 11 : 181 - 186
  • [3] Influence of Al-Si alloy microstructure on the corrosion resistance of coatings formed by the microarc oxidation method
    Dudareva, Natalia Y.
    Kalschikov, Roman V.
    Zaynullina, Liliya I.
    INTERNATIONAL CONFERENCE ON MODERN TRENDS IN MANUFACTURING TECHNOLOGIES AND EQUIPMENT (ICMTMTE 2017), 2017, 129
  • [4] EFFECTS OF PRE-OXIDATION ON HOT CORROSION RESISTANCE OF Al-Si COATINGS
    Lv, Haishuang
    Li, Yanmei
    Li, Yabin
    Fan, Naiwen
    MATERIALI IN TEHNOLOGIJE, 2023, 57 (01): : 49 - 56
  • [5] Influence of Si Content on the Microstructure and Corrosion Behavior of Additive Manufactured Al-Si Alloys
    Revilla, Reynier I.
    De Graeve, Iris
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2018, 165 (13) : C926 - C932
  • [6] Computer simulation of the cyclic oxidation of the Al-Si coatings
    Luo, JH
    Zhang, Q
    Song, FB
    COMPUTATIONAL MATERIALS SCIENCE, 2004, 31 (3-4) : 220 - 224
  • [7] Influence of calcium on the morphology and corrosion performance of hot-dip Al-Si coatings
    Grandhi, Srinivasulu
    Oh, Min-Suk
    MATERIALS LETTERS, 2023, 353
  • [8] High temperature oxidation properties of Al-Si coatings on a DZ4 supperalloy
    College of Materials Science and Chemical Engineering, Harbin Engineering University, Harbin 150001, China
    Harbin Gongcheng Daxue Xuebao, 2008, 9 (997-1000):
  • [9] Al, Si, and Al-Si Coatings to Improve the High-Temperature Oxidation Resistance of AISI 304 Stainless Steel
    Zandrahimi, Morteza
    Vatandoost, Javad
    Ebrahimifar, Hadi
    OXIDATION OF METALS, 2011, 76 (3-4): : 347 - 358
  • [10] Corrosion protection properties of anodic oxide coatings on an Al-Si alloy
    Li, X
    Nie, X
    Wang, L
    Northwood, DO
    SURFACE & COATINGS TECHNOLOGY, 2005, 200 (5-6): : 1994 - 2000
12345