Structural, magnetic and magnetocaloric properties in La 0.5-xRexCa0.5MnO3 manganites (x = 0; 0.1 and Re = Gd, Eu and Dy)

被引：0
|
作者：
机构：
[1] Krichene, A.
[2] Boujelben, W.
[3] 1,Cheikhrouhou, A.
来源：
Boujelben, W. (Wahibaboujelben@yahoo.fr) | 1600年 / Elsevier Ltd卷 / 550期
关键词：
Structural; magnetic and magnetocaloric properties of the compounds La 0.5-xRexCa0.5MnO3 (x = 0; 0.1 and Re = Gd; Eu and Dy) powder samples have been investigated. All our samples were synthesized using the solid state reaction at high temperature. All the samples are single phase and crystallize with Pnma space group. Magnetization measurements versus temperature in a magnetic applied field of 0.05 T show that all our substituted La0.4Re0.1Ca0.5MnO 3 (Re = Gd; Eu and Dy) samples exhibit a paramagnetic (PM) to ferromagnetic (FM) transition when temperature decreases. The lanthanum substitution by Re induces a decrease of the TC value as well as the destruction of the phase-separated state existing at low temperature in the parent compound La0.5Ca0.5MnO3. Field dependence of magnetization shows that all our samples are phase-separated ones even above TC. The absolute values of magnetic entropy change |ΔSM| for a magnetic applied field of 2 T for the doped samples are 0.78; 1.15 and 2.16 J kg-1 K-1 for Re = Gd; Eu and Dy respectively at the Curie temperature TC. The maximum values of |ΔSM| decrease with σ2 but La 0.4Dy0.1Ca0.5MnO3 shows a different behavior that may be due to the huge magnetic moment of Dy3+ ion. All the substituted specimens show some anomalies in the temperature dependence of magnetic entropy change curves only for the high values of magnetic field which can be attributed to the metamagnetic transition. Arrott plots show that the substituted specimens exhibit a second-ordered transition from PM to FM state unlike the metamagnetic transition which is first order. © 2012 Elsevier B.V. All rights reserved;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Journal article (JA)
引用
收藏
相关论文
共 50 条
12345