Preparation and Properties of Polyimide Nanofibers

被引：0
|
作者：
Shen Y. [1 ]
Li D. [1 ]
Liu Q. [1 ]
Deng B. [1 ]
机构：
[1] Key Laboratory of Eco-Textiles, Jiangnan University, Ministry of Education, Wuxi
来源：
Gaofenzi Cailiao Kexue Yu Gongcheng/Polymeric Materials Science and Engineering | 2020年 / 36卷 / 01期
关键词：
Electrospinning; Polyimide; Properties; Structures;
D O I：
10.16865/j.cnki.1000-7555.2019.0356
中图分类号：
学科分类号：
摘要：
In order to study the structures and properties of polyimide (PI) nanofibers spun by "one-step method", two kinds of PI nanofibers, of which the average fiber diameter ranges from 0.364 μm to 0.785 μm, were prepared through electrospinning technology by using thermoplastic polyimide powder as raw material, and a mixture of N, N-dimethylformamide (DMF), N, N-dimethylacetamide (DMAc) or Tween 80 as solvent. The structures and properties of PI nanofibers were characterized. The results are as follows. The surface of nanofiber has no microholes. The fiber diameter increases with the polymer concentration increased, and reduces first and then increases with the spinning voltage and tip-to-collector distance increased. In addition, the solvent has significant influence on the chemical structure and thermodynamic performance of PI nanofibers. The structure regularity, mechanical property (stress of 24.8 MPa) and thermal stability (thermal decomposing temperature of 535℃) of PIDMF-DMAc are higher than those of PITween80-DMF-DMAc nanofiber (the stress and thermal decomposing temperature are 16.5 MPa and 421℃, respectively). © 2020, Editorial Board of Polymer Materials Science & Engineering. All right reserved.
引用
收藏
页码：44 / 49
页数：5
相关论文
共 12 条
  • [1] Ding M.X., Isomeric polyimide, Prog. Polym. Sci., 32, pp. 623-668, (2007)
  • [2] Gong G., Wu J., Novel polyimide materials produced byelectrospinning, Prog. Chem., 23, pp. 750-759, (2011)
  • [3] Ding Y.C., Hou H.Q., Zhao Y., Et al., Electrospun polyimidenanofibers and their applications, Prog. Polym. Sci., 61, pp. 67-103, (2016)
  • [4] Jiang S.H., Duan G.G., Chen L.L., Et al., Mechanical performance of aligned electrospun polyimide nanofiber belt at high temperature, Mater. Lett., 140, pp. 12-15, (2015)
  • [5] Li X.J., Functionalization and properties of polyimide nanofibers, (2015)
  • [6] Chen J., Zhang D.J., Zhang T.J., Et al., Preparation of thermoplastic polyimide ultrafine fiber nonwoven by electrospinning, Journal of Materials Engineering, 46, 2, pp. 41-49, (2018)
  • [7] Zhu J.H., Wei S.Y., Chen X.L., Et al., Electrospun polyimide nanocomposite fibers reinforced with core-shell Fe-FeO nanoparticles, J. Phys. Chem., C, 114, 2, pp. 8844-8850, (2010)
  • [8] Liu C.K., Research progress of electrospinning, China Synthetic Fiber Industry, 35, 2, pp. 53-56, (2012)
  • [9] Thenmozhi S., Dharmaraj N., Kadirvelu K., Et al., Electrospunnanofibers: New generation materials for advanced applications, Mater. Sci. Eng., B, 217, pp. 36-48, (2017)
  • [10] Li Z., Wang J., Influencing factors of electrospinning spinnability, Synthetic Fiber, 37, 9, pp. 6-11, (2008)
12