Enhancing fabrication of hybrid microfluidic devices through silane-based bonding: A focus on polydimethylsiloxane-cyclic olefin copolymer and PDMS-lithium niobate

被引：1

作者：

Agha, Abdulrahman ^{[1
]}

Dawaymeh, Fadi ^{[2
]}

Alamoodi, Nahla ^{[2
,3
]}

Alazzam, Anas ^{[1
,3
]}

机构：

[1] Department of Mechanical and Nuclear Engineering, Khalifa University, Abu Dhabi, United Arab Emirates

[2] Department of Chemical Engineering, Khalifa University, Abu Dhabi, United Arab Emirates

[3] System on Chip Lab, Khalifa University, Abu Dhabi, United Arab Emirates

来源：

Applied Research | 2024年 / 3卷 / 04期

关键词：

Chemical activation - Chemical bonds - Contact angle - Cost effectiveness - Coupling agents - Fabrication - Fluidic devices - Lithium - Lithium compounds - Microchannels - Niobium compounds - Polydimethylsiloxane - Scanning electron microscopy - Silicones - Tensile strength - Tensile testing;

D O I：

10.1002/appl.202300116

中图分类号：

学科分类号：

摘要：

Effective manipulation and control of fluids in microfluidic channels requires robust bonding between the different components. Polydimethylsiloxane (PDMS) is widely employed in microchannel fabrication due to its affordability, biocompatibility, and straightforward fabrication process. However, PDMS's low surface energy poses challenges in bonding with many organic and inorganic substrates, hindering the development of hybrid microfluidic devices. In this study, a simple and versatile three step process is presented for bonding PDMS microchannels with organic (cyclic olefin copolymer (COC)) and inorganic substrates (lithium niobate (LiNbO3)) using plasma activation and a silane coupling agent. Initially, the PDMS surface undergoes oxygen/argon plasma activation, followed by functionalization with (3-aminopropyl) triethoxysilane (APTES). Subsequently, the COC or LiNbO3 is plasma activated and brought into contact with PDMS under a load at a specific temperature. Characterization by Fourier transform infrared, scanning electron microscopy, atomic force microscopy, and contact angle measurements confirmed the successful treatment of the substrates. In addition, bonding strength of the fabricated hybrid devices was assessed through leakage and tensile tests. Under optimized conditions (100°C and 4% v/v APTES), PDMS-COC hybrid microchannels achieved a flow rate of 600 mL/h without leakage and a tensile strength of 562 kPa. Conversely, the PDMS- LiNbO3 assembly demonstrated a flow rate of 216 mL/h before leakage, with a tensile strength of 334 kPa. This bonding method exhibits significant potential and versatility for various materials in microfluidic applications, ranging from biomedical research to enhanced oil recovery. © 2024 The Authors. Applied Research published by Wiley-VCH GmbH.