Annealing process and microstructure evolution of cold-rolled low-carbon medium-manganese TRIP steels

被引：0

作者：

Li, Zhen ^{[1
]}

Cheng, Xiao-Jie ^{[1
]}

Cai, A-Yun ^{[1
]}

Wen, Da ^{[1
]}

Shi, Jing ^{[1
]}

Zhao, Ai-Min ^{[2
]}

机构：

[1] Beijing Shougang Cold Rolling Co Ltd, Beijing, China

[2] Engineering Research Institute, University of Science and Technology Beijing, Beijing, China

来源：

Cailiao Rechuli Xuebao/Transactions of Materials and Heat Treatment | 2014年 / 35卷 / 07期

关键词：

Annealing - Cold rolling - Low carbon steel - Plasticity - Steel sheet - Tensile strength - Metal cladding - Austenite - High strength steel;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

The effects of annealing process on mechanical properties and the stability of retained austenite of third generation of AHSS of cold-rolled low-carbon medium-manganese TRIP steels were investigated. The results show that the mechanical properties are significantly influenced by intercritical annealing temperature and soaking time. When the samples of 6.72%Mn-TRIP steel are annealed at approximately 590 for 18 h, the tensile strength is 815 MPa and the elongation is 38%, the UTS×TE values in excess of 30 GPa·% can be obtained. During the intercritical soaking time, C and Mn atoms in the martensite have partitioned into retained austenite, thereby, the retained austenite can be stabilized at room temperature. Due to the combination of the retained austenite, martensitic and recrystallization ferrite, that the remarkable combinations of strength and ductility are obtained.

引用

页码：151 / 155

共 50 条

[1] Microstructure and Mechanical Properties of Hot-Rolled Low-Carbon Medium-Manganese TRIP Steels
Li, Zhen
Zhao, Aimin
Tang, Di
Li, Benhai
[J]. ADVANCED ENGINEERING MATERIALS, PTS 1-3, 2011, 194-196 : 127 - +
[2] ANNEALING BEHAVIOR OF COLD-ROLLED LOW-CARBON STEELS
GROF, L
ARATO, P
BOC, I
KAJDI, K
NADOR, B
[J]. METAL SCIENCE, 1983, 17 (09): : 451 - 455
[3] Effect of annealing time on the microstructure and mechanical properties of a cold rolled medium-manganese TRIP steel
[J]. Zhao, A.-M. (aimin.zhao@ustb.edu.cn), 1600, University of Science and Technology Beijing (35):
[4] DETERMINATION OF SURFACE CARBON IN LOW-CARBON COLD-ROLLED STEELS
ZAMARAEV, VP
ORZHEKHOVSKAYA, AI
TOLSTOVA, EA
PARSADANOV, VG
MACHEVSKAYA, RA
[J]. INDUSTRIAL LABORATORY, 1989, 55 (04): : 385 - 387
[5] THE EFFECTS OF MANGANESE AND NITROGEN ON THE RECRYSTALLIZATION TEXTURES IN COLD-ROLLED VERY LOW-CARBON STEELS
TAGASHIRA, K
HUTCHINSON, B
DILLAMORE, I
[J]. TRANSACTIONS OF THE JAPAN INSTITUTE OF METALS, 1985, 26 (02): : 79 - 87
[6] Effect of annealing process on microstructure and mechanical property of medium-manganese TRIP steel
Wang, Xu-ming
Zhao, Ai-min
Chen, Shan-shan
Bao, Zhi-yi
[J]. INTERNATIONAL JOURNAL OF MATERIALS & PRODUCT TECHNOLOGY, 2022, 64 (3-4): : 265 - 277
[7] Influence of state of Nb on recrystallization temperature during annealing in cold-rolled low-carbon steels
Ogawa, Toshio
Sugiura, Natsuko
Maruyama, Naoki
Yoshinaga, Naoki
[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2013, 564 : 42 - 45
[8] Rapid transformation annealing: A novel method for grain refinement of cold-rolled low-carbon steels
Lesch, C.
Alvarez, P.
Bleck, W.
Gil Sevillano, J.
[J]. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2007, 38A (09): : 1882 - 1890
[9] Rapid Transformation Annealing: a Novel Method for Grain Refinement of Cold-Rolled Low-Carbon Steels
C. Lesch
P. Álvarez
W. Bleck
J. Gil Sevillano
[J]. Metallurgical and Materials Transactions A, 2007, 38 : 1882 - 1890
[10] Ferrite recrystallization and austenite formation at the early stage of annealing in cold-rolled low-carbon steels
Ogawa T.
[J]. International Journal of Mechanical and Materials Engineering, 2015, 10 (1)

← 1 2 3 4 5 →