Effects of heat treatment on microstructure and magnetic properties of (Fe0.52Co0.30Ni0.18)73Cr17Zr10 amorphous alloy

被引：0
|
作者：
Xie C.-X. [1 ]
Zhong S.-Y. [1 ]
Yang Y.-Z. [2 ]
Luo J.-Y. [1 ]
Liao Z.-L. [1 ]
机构：
[1] School of Mechanical Engineering, Dongguan University of Technology, Dongguan, 523808, Guangdong
[2] Faculty of Materials and Energy, Guangdong University of Technology, Guangzhou
来源：
Xie, Chun-Xiao (xiechx@dgut.edu.cn) | 1600年 / Beijing Institute of Aeronautical Materials (BIAM)卷 / 44期
关键词：
Fe-based amorphous alloy; Heat treatment; Magnetic property; Microstructure;
D O I：
10.11868/j.issn.1001-4381.2016.08.008
中图分类号：
学科分类号：
摘要：
(Fe0.52Co0.30Ni0.18)73Cr17Zr10 amorphous ribbons were prepared by melt-spun method and annealed at different temperatures. X-ray diffraction, atomic force microscopy and vibrating sample magnetometer were adopted to study the effect of annealing temperature on the microstructure and magnetic properties of this alloy. The results show that the crystallization process of this alloy is amorphous→α-Fe(Co)+amorphous' →α-Fe(Co)+Cr2Ni3+Fe3Ni2+Cr2Zr+unidentified phase. When annealing temperature Ti is lower than Tg, the Ms increases slightly as a result of relaxation of the internal stress of the as-quenched amorphous alloy. When Ti is in between Tx and Tp1, the Ms significantly increases due to the partial crystallization of amorphous precursors to create a homogeneous distribution of α-Fe(Co) nanocrystals within a residual amorphous matrix. When Ti is higher than Tp1, the Ms drops rapidly, which may be caused by the grain growth and the formation of paramagnetic phase. This alloy after annealed at 565℃ has the best magnetic property (Ms=106.8A·m2·kg-1). The results of AFM observation show that in the annealed amorphous ribbons the grain size measured from AFM graphs is much larger than that of the α-Fe(Co) nanocrystal size caculated by Scherrer method, which is a typical phenomenon of coated grain. © 2016, Journal of Materials Engineering. All right reserved.
引用
收藏
页码：46 / 50
页数：4
相关论文
共 17 条
  • [1] Li X., Makino A., Yubuta K., Et al., Mechanical properties of soft magnetic (Fe<sub>0.76</sub>Si<sub>0.096</sub> B<sub>0.084</sub>P<sub>0.06</sub>)<sub>(100-x)</sub>Cu<sub>x</sub>(x=0 and 0.1) bulk glassy alloys, Materials Transactions, 50, 6, pp. 1286-1289, (2009)
  • [2] Yao K.F., Zhang C.Q., Fe-based bulk metallic glass with high plasticity, Appl Phys Lett, 90, 6, (2007)
  • [3] Lee K.B., Park K.W., Yi S.H., Et al., Fe-based amorphous alloy with high strength and toughness synthesized based on nm-scale phase separation, Journal of Metals and Materials, 48, 1, pp. 1-7, (2010)
  • [4] Guo S.F., Liu L., Li N., Et al., Fe-based bulk metallic glass matrix composite with large plasticity, Scripta Materialia, 62, 6, pp. 329-332, (2010)
  • [5] Bitoh T., Makino A., Inoue A., Et al., Large bulk soft magnetic[(Fe<sub>0.5</sub>-Co<sub>0.5</sub>)<sub>0.75</sub>B<sub>0.2</sub>Si<sub>0.05</sub>]<sub>96</sub>Nb<sub>4</sub> glassy alloy prepared by B<sub>2</sub>O<sub>3</sub> flux melting and water quenching, Appl Phys Lett, 88, 18, (2006)
  • [6] Long Z.L., Shao Y., Xie G.Q., Et al., Enhanced soft-magnetic and corrosion properties of Fe-based bulk glassy alloys with improved plasticity through the addition of Cr, Journal of Alloys and Compounds, 462, 1-2, pp. 52-59, (2008)
  • [7] Liu F.M., Zhang H.Y., Zhang T., Glass forming ability and magnetic properties of Fe-Nd-B-Zr bulk metallic glasses, Journal of Materials Engineering, 10, pp. 6-10, (2014)
  • [8] Yao J.H., Wang J.Q., Li Y., Et al., Ductile Fe-Nb-B bulk metallic glass with ultrahigh strength, Applied Physics Letters, 92, 25, (2008)
  • [9] Wang J.F., Li R., Hua N.B., Et al., Ternary Fe-P-C bulk metallic glass with good soft-magnetic and mechanical properties, Scripta Materialia, 65, 6, pp. 536-539, (2011)
  • [10] Eckert J., Das J., Mechanical properties of bulk metallic glasses and composites, J Mater Res, 22, 2, pp. 285-301, (2007)
12