Mechanical properties of 7N01 aluminum friction stir welding joint

被引：0

作者：

Meng, Lichun ^{[1
]}

Kang, Xu ^{[2
,3
]}

Sun, Yanjun ^{[2
]}

Sun, Kai ^{[2
]}

Shi, Qingyu ^{[2
]}

机构：

[1] CSR Sifang Locomotive and Rolling Stock. Co. Ltd., Qingdao 266111, China

[2] Key Laboratory for Advanced Materials Processing Technology of Education Ministry, Department of Mechanical Engineering, Tsinghua University, Beijing 100084, China

[3] The Locomotive and Car Research Institute, China Academy of Railway Science, Beijing 100081, China

来源：

Hanjie Xuebao/Transactions of the China Welding Institution | 2012年 / 33卷 / 02期

关键词：

Hardness - Fracture - Friction - Research laboratories - Tensile strength - Aluminum alloys - Tensile testing - Tribology;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Mechanical properties of friction stir welded 7N01 aluminum joint under different welding parameters have been studied in this paper. The tensile test results showed that, with a certain rotational speed and welding speed, the FSW joints could keep at a high strength level of 340 MPa even the plunge depth varied from 0.3 to 1.0 mm. SEM was carried and the FSW joints exhibited mainly dimpled fracture surfaces. Hardness of the joints was also measured. The hardness in retreating side was a little higher than that of advancing side. This result corresponded well with the tensile test result. Fracture occurred at the advancing side in tensile test.

引用

页码：90 / 92

共 50 条

[1] Stress corrosion behavior of friction stir welding joint of 7N01 aluminum alloy
Pan, Yuzhe
Wang, Yu
Guo, Fuqiang
Zhang, Tiehao
Matsuda, Kenji
Wu, Dongting
Zhang, Yongang
Zou, Yong
JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2021, 15 (15): : 1130 - 1144
[2] Investigation of void formation in friction stir welding of 7N01 aluminum alloy
Zhao, Yingxin
Han, Jianmin
Domblesky, Joseph P.
Yang, Zhiyong
Li, Zhiqiang
Liu, Xiaolong
JOURNAL OF MANUFACTURING PROCESSES, 2019, 37 : 139 - 149
[3] Investigation of through thickness microstructure and mechanical properties in friction stir welded 7N01 aluminum alloy plate
Zhao, Yingxin
Yang, Zhiyong
Domblesky, Joseph P.
Han, Jianmin
Li, Zhiqiang
Liu, Xiaolong
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2019, 760 : 316 - 327
[4] Effect of repair welding on microstructure and mechanical properties of 7N01 aluminum alloy MIG welded joint
Li, Shuai
Dong, Honggang
Wang, Xingxing
Liu, Zhongying
Tan, Zhaojun
Shangguan, Linjian
Lu, Quanbin
Zhong, Sujuan
JOURNAL OF MANUFACTURING PROCESSES, 2020, 54 : 80 - 88
[5] Effect of Repair Welding on Corrosion Behavior of 7N01 Aluminum Alloy Welded Joint
Li Shuai
Liu Zhongying
Wang Xingxing
Mao Feng
Xia Yueqing
Jiu Yongtao
Shangguan Linjian
Long Weimin
RARE METAL MATERIALS AND ENGINEERING, 2021, 50 (03) : 762 - 768
[6] Effect of Service on Fracture Mechanical Properties of 7N01 Aluminum Alloy
Zhang X.-C.
Xie L.-Y.
Hu J.-X.
Zhang S.-J.
Dongbei Daxue Xuebao/Journal of Northeastern University, 2017, 38 (10): : 1442 - 1446
[7] Effect of in-situ ZrB2 nanoparticles on microstructure and mechanical properties of friction stir welding joints in 7N01 matrix composites
Cao, Rui
Kai, Xizhou
Qian, Wei
Wang, Tao
Peng, Qiang
Zhao, Yutao
MATERIALS CHARACTERIZATION, 2024, 207
[8] Effect of Repair Welding on Corrosion Behavior of 7N01 Aluminum Alloy Welded Joint
Li, Shuai
Liu, Zhongying
Wang, Xingxing
Mao, Feng
Xia, Yueqing
Jiu, Yongtao
Shangguan, Linjian
Long, Weimin
Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2021, 50 (03): : 762 - 768
[9] Microstructures and mechanical properties of friction stir welding joint of 2014 aluminum alloy
State Key Lab. of Advanced Welding Production Technology, Harbin Institute of Technology, Harbin 150001, China
不详
Hangkong Cailiao Xuebao, 2006, 1 (67-70):
[10] Structure and properties of friction stir welding joint of aluminum profile
Hanjie Xuebao/Transactions of the China Welding Institution, 2023, 44 (11): : 124 - 128

← 1 2 3 4 5 →