Microstructure and Joining Properties of High Nb-containing TiAl Alloy Brazed Joints

被引：0
|
作者：
高铌TiAl合金钎焊接头组织和性能研究
机构：
[1] Song, Xiaoguo
[2] Si, Xiaoqing
[3] Cao, Jian
[4] Wang, Zhiquan
[5] Zhao, Hongyun
[6] Feng, Jicai
来源：
Song, Xiaoguo (songxg@hitwh.edu.cn) | 2018年 / Science Press卷 / 47期
基金：
中国国家自然科学基金;
关键词：
D O I：
暂无
中图分类号：
学科分类号：
摘要：
High Nb-containing TiAl alloy (Ti-45Al-8.5Nb-(W, B, Y) (at%), abbreviated as TAN alloy) was brazed at 1100℃ using Ti-28Ni (wt%) eutectic brazing alloy. The typical interfacial microstructure was TAN/τ3-Al3Ti2Ni+B2/α2-Ti3Al layer/α2-Ti3Al + δ-Ti2Ni/α2-Ti3Al layer/τ3-Al3Ti2Ni + B2/TAN. The effects of holding time on interfacial microstructure and joining properties of TAN brazed joints were investigated. The results demonstrate that the diffusion of Ni from molten brazing alloy to TAN substrate plays an important role in the interfacial microstructure evolution, which results in an increase of diffusion zone and a reduction of brazed seam with the prolongation of holding time. Shear test indicates that the maximum shear strength at room temperature and high temperature (600℃) reaches 248.6 MPa and 166.4 MPa, respectively when holding time is 15 min. Fracture analyses reveal that brittle fracture prefers to initiate and propagate in the continuous intermetallic layers during shear test. Copyright © 2018, Northwest Institute for Nonferrous Metal Research. Published by Elsevier BV. All rights reserved.
引用
收藏
相关论文
共 50 条
  • [1] Microstructure and Joining Properties of High Nb-containing TiAl Alloy Brazed Joints
    Song Xiaoguo
    Si Xiaoqing
    Cao Jian
    Wang Zhiquan
    Zhao Hongyun
    Feng Jicai
    RARE METAL MATERIALS AND ENGINEERING, 2018, 47 (01) : 52 - 58
  • [2] Hierarchical microstructure in high Nb-containing TiAl alloy
    He, Neng
    Quan, Maohua
    Lin, Junpin
    He, Lianlong
    Hu, Changyi
    MATERIALS CHARACTERIZATION, 2021, 171
  • [3] Microstructure optimization and improved tensile property in a high Nb-containing γ-TiAl alloy
    Dai, Chengren
    Sun, Jian
    MATERIALS CHARACTERIZATION, 2022, 185
  • [4] Microstructure and mechanical properties of TiAl/TiAl joints brazed with a newly developed Ti–Ni–Nb–Zr quaternary filler alloy
    H.S.Ren
    Y.L.Shang
    X.Y.Ren
    Y.J.Jing
    H.P.Xiong
    Y.Y.Cheng
    Progress in Natural Science:Materials International, 2022, 32 (06) : 758 - 768
  • [5] Continuous cooling transformation (CCT) behavior of a high Nb-containing TiAl alloy
    Yang, Jieren
    Cao, Bei
    Wu, Yulun
    Gao, Zitong
    Hu, Rui
    MATERIALIA, 2019, 5
  • [6] Microstructure and mechanical properties of TiAl/TiAl joints brazed with a newly developed Ti-Ni-Nb-Zr quaternary filler alloy
    Ren, H. S.
    Shang, Y. L.
    Ren, X. Y.
    Jing, Y. J.
    Xiong, H. P.
    Cheng, Y. Y.
    PROGRESS IN NATURAL SCIENCE-MATERIALS INTERNATIONAL, 2022, 32 (06) : 758 - 768
  • [7] High temperature deformation behavior of near γ-phase high Nb-containing TiAl alloy
    Li, Jianbo
    Liu, Yong
    Liu, Bin
    Wang, Yan
    Cao, Peng
    Zhou, Canxu
    Xiang, Chunjie
    He, Yuehui
    INTERMETALLICS, 2014, 52 : 49 - 56
  • [8] Precipitation behaviors in a quenched high Nb-containing TiAl alloy during annealing
    Song, Lin
    Hu, Xingguo
    Zhang, Tiebang
    Li, Jinshan
    INTERMETALLICS, 2017, 89 : 79 - 85
  • [9] Interfacial microstructure and joining properties of TiAl/Si3N4 brazed joints
    Song, X. G.
    Cao, J.
    Li, C.
    Feng, J. C.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2011, 528 (22-23): : 7030 - 7035
  • [10] Ordinary dislocation configurations in high Nb-containing TiAl alloy deformed at high temperatures
    Song, Lin
    Lin, Junpin
    Li, Jinshan
    PHILOSOPHICAL MAGAZINE, 2017, 97 (07) : 515 - 526
12345