Microstructural evolution of heat-resistant steel Super304H during 650°C long term aging

被引：0
|
作者：
Yu, Hong-Yao [1 ]
Chi, Cheng-Yu [1 ]
Dong, Jian-Xin [1 ]
Xie, Xi-Shan [1 ]
Cui, Zheng-Qiang [2 ]
Chen, Xiao-Fang [2 ]
机构：
[1] School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China
[2] Shanghai Power Equipment Research Institute, Shanghai 200240, China
来源：
Beijing Keji Daxue Xuebao/Journal of University of Science and Technology Beijing | 2010年 / 32卷 / 07期
关键词：
D O I：
暂无
中图分类号：
学科分类号：
摘要：
12
引用
收藏
页码：877 / 882
相关论文
共 50 条
  • [1] Microstructure of Super304H austenitic heat-resistant steel after long-term aging
    Sun, J. (jsun@sjtu.edu.cn), 1600, Editorial Office of Transactions of Materials and Heat Treatment (35):
  • [2] Strengthening effect of precipitate phase in Super304H austenitic heat-resistant steel after long-term aging
    Zhan, Qian (qzhan@mater.ustb.edu.cn), 1600, Central South University of Technology (24):
  • [3] Effect of Nb on the microstructural evolution and microhardness of Super304H austenitic stainless steel weld metals during long-term aging
    Xiao, Xiaopeng
    Li, Dianzhong
    Li, Yiyi
    Lu, Shanping
    INTERNATIONAL JOURNAL OF MATERIALS RESEARCH, 2022, 113 (01) : 33 - 43
  • [4] Microstructural Evolution and the Effect on Mechanical Properties of S30432 Heat-resistant Steel during Aging at 650°C
    Zhang, Yujie
    Zhu, Lihui
    Qi, Anfang
    Lu, Zhengran
    ISIJ INTERNATIONAL, 2010, 50 (04) : 596 - 600
  • [5] Microstructure and properties of Super304H austenitic heat-resistant steel after service for 36891 h
    Wang, Wei
    Huang, Xiang
    Cai, Yong-Jiang
    Li, Wen-Sheng
    Gao, Yan
    Cailiao Rechuli Xuebao/Transactions of Materials and Heat Treatment, 2015, 36 (10): : 89 - 94
  • [6] Processing maps and hot workability of Super304H austenitic heat-resistant stainless steel
    Tan, Shuping
    Wang, Zhenhua
    Cheng, Shichang
    Liu, Zhengdong
    Han, Jiecai
    Fu, Wantang
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2009, 517 (1-2): : 312 - 315
  • [7] Strengthening and Embrittling Mechanism of Super 304H Steel during Long-Term Aging at 650 °C
    Wu, Yue
    Chai, Fufangzhuo
    Liu, Junjian
    Wang, Jiaqing
    Li, Yong
    Du, Chengchao
    MATERIALS, 2024, 17 (03)
  • [8] Long-term degradation behavior of slurry aluminide coating on Super304H stainless steel at 650 °C
    Lu, Jintao
    Huang, Jinyang
    Wang, Jiangwei
    Yang, Zhen
    Gu, Yuefeng
    CORROSION SCIENCE, 2021, 178
  • [9] Precipitation Kinetics of M23C6 Carbides in the Super304H Austenitic Heat-Resistant Steel
    Qingwen Zhou
    Shaobo Ping
    Xiaobo Meng
    Ruikun Wang
    Yan Gao
    Journal of Materials Engineering and Performance, 2017, 26 : 6130 - 6139
  • [10] Precipitation Kinetics of M23C6 Carbides in the Super304H Austenitic Heat-Resistant Steel
    Zhou, Qingwen
    Ping, Shaobo
    Meng, Xiaobo
    Wang, Ruikun
    Gao, Yan
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2017, 26 (12) : 6130 - 6139
12345