Achieving room temperature superplasticity in Zn-5Al alloy at high strain rates by equal-channel angular extrusion

被引：0
|
作者：
机构：
[1] Demirtas, M.
[2] Purcek, G.
[3] Yanar, H.
[4] Zhang, Z.J.
[5] Zhang, Z.F.
来源：
Purcek, G. | 1600年 / Elsevier Ltd卷 / 623期
关键词：
Multi-pass equal-channel angular extrusion/pressing (ECAE/P) was applied to the eutectic Zn-5Al alloy to achieve high strain-rate (HSR) superplasticity in that alloy at room temperature (RT) by producing ultrafine-grained (UFG) microstructure. ECAE processing transformed the coarse-grained lamellar/spherical microstructure into a unique bimodal structure having equiaxed Zn-rich η-phase with a mean grain size of 540 nm and spherical Al-rich α-phase with an average grain size of 110 nm. The α-phase particles accumulated mainly along the η-phase boundaries. This unique microstructure brought about an extraordinary improvement in HSR superplasticity of the alloy even at RT. While the strength values decreased after ECAE; the elongation to failure increased substantially. The maximum elongation was 520% at the strain rate of 10-3 s-1; still high elongation of about 400% was achieved at a high strain rate of 10-2 s-1. This extraordinary improvement in HSR superplasticity of Zn-5Al alloy was attributed to the morphologically unique bimodal microstructure in UFG regime formed after ECAE. The grain boundary sliding (GBS) was found to be the main deformation mechanism for this alloy in superplastic regime. © 2014 Elsevier B.V;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Journal article (JA)
引用
收藏
相关论文
共 50 条
  • [1] Achieving room temperature superplasticity in Zn-5Al alloy at high strain rates by equal-channel angular extrusion
    Demirtas, M.
    Purcek, G.
    Yanar, H.
    Zhang, Z. J.
    Zhang, Z. F.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2015, 623 : 213 - 218
  • [2] High strain rate superplasticity in an Al-Li-Mg alloy subjected to equal-channel angular extrusion
    Musin, F
    Kaibyshev, R
    Motohashi, Y
    Sakuma, T
    Itoh, G
    MATERIALS TRANSACTIONS, 2002, 43 (10) : 2370 - 2377
  • [3] Superplasticity at room temperature in Zn-22Al alloy processed by equal-channel-angular extrusion
    Tanaka, T
    Higashi, K
    MATERIALS TRANSACTIONS, 2004, 45 (04) : 1261 - 1265
  • [4] Improvement of high strain rate and room temperature superplasticity in Zn-22Al alloy by two-step equal-channel angular pressing
    Demirtas, M.
    Purcek, G.
    Yanar, H.
    Zhang, Z. J.
    Zhang, Z. F.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2015, 620 : 233 - 240
  • [5] High strain rate superplasticity in a Zn-22% Al alloy after equal-channel angular pressing
    Lee, SM
    Langdon, TG
    SUPERPLASTICITY IN ADVANCED MATERIALS, ICSAM-2000, 2001, 357-3 : 321 - 326
  • [6] Achieving superplasticity at high strain rates using equal channel angular pressing
    Furukawa, M
    Horita, Z
    Nemoto, M
    Langdon, TG
    MATERIALS SCIENCE AND TECHNOLOGY, 2000, 16 (11-12) : 1330 - 1333
  • [7] Effect of equal-channel angular pressing on room temperature superplasticity of quasi-single phase Zn-0.3Al alloy
    Demirtas, M.
    Purcek, G.
    Yanar, H.
    Zhang, Z. J.
    Zhang, Z. F.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2015, 644 : 17 - 24
  • [8] Achievement of low temperature superplasticity in a commercial aluminium alloy processed by equal-channel angular extrusion
    Musin, F
    Kaibyshev, R
    Motohashi, Y
    Itoh, G
    SUPERPLASTICITY IN ADVANCED MATERIALS, 2003, 447-4 : 465 - 470
  • [9] Achieving high strain rate superplasticity in an At-Li-Mg alloy through equal channel angular extrusion
    Kaibyshev, R
    Shipilova, K
    Musin, F
    Motohashi, Y
    MATERIALS SCIENCE AND TECHNOLOGY, 2005, 21 (04) : 408 - 418
  • [10] Achieving room temperature superplasticity in the Zn-0.5Cu alloy processed via equal channel angular pressing
    Bednarczyk, Wiktor
    Kawalko, Jakub
    Watroba, Maria
    Bala, Piotr
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2018, 723 : 126 - 133
12345