Intrinsic coercivity of SmCo based permanent magnetic films prepared on hot substrates at 650℃

被引：0

作者：

Li, Yuanxun ^{[1
]}

Peng, Long ^{[2
]}

机构：

[1] State Key Laboratory of Electronic Thin Films and Integrated Devices, University of Electronic Science and Technology of China, Chengdu,610054, China

[2] Chengdu University of Information Technology, Chengdu,610225, China

来源：

Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering | 2015年 / 44卷 / 04期

关键词：

Chromium - Cobalt alloys - Coercive force - Metallic films - Temperature distribution - Binary alloys - Film preparation - Substrates - Film thickness - Rare earths - Samarium alloys - Molybdenum - Magnetism - Magnetic multilayers;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

The intrinsic coercivity of the SmCo based permanent magnetic films prepared on the hot Si substrate at 650℃ with Al, Cu, Ag, Mo, and Cr underlayer without a subsequent annealing process was investigated. The results show that the films with Mo and Cr underlayer provide an improved intrinsic coercivity. The film thickness presents a complex effect on the intrinsic coercivity of the films with Mo underlayer. When the film thickness is 3.0 µm, the maximum value of the intrinsic coercivity is 281.6 kA·m-1 at room temperature. Furthermore, the temperature dependence of intrinsic coercivity is found to be strongly correlated with the magnetic parameters. In the range from 25℃ to 300℃, the intrinsic coercivity of the films of above 200 kA·m-1 is obtained. Copyright © 2015, Northwest Institute for Nonferrous Metal Research. Published by Elsevier BV. All rights reserved.

引用

页码：796 / 799

共 50 条

[1] Intrinsic Coercivity of SmCo Based Permanent Magnetic Films Prepared on Hot Substrates at 650 °C
Li Yuanxun
Peng Long
RARE METAL MATERIALS AND ENGINEERING, 2015, 44 (04) : 796 - 799
[2] Improved magnetic properties of SmCo-based films deposited on hot Si substrates
Li, Yuanxun
Peng, Long
JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2012, 324 (12) : 1967 - 1969
[3] Microstructure, phase compositions, and coercivity evolution in micron-thick SmCo-based permanent magnetic films
Qiu, Zhaoguo (zgqiu@scut.edu.cn), 1600, Elsevier Ltd (1010):
[4] Coercivity in SmCo hard magnetic films for MEMS applications
Pina, E
Palomares, FJ
García, MA
Cebollada, F
de Hoyos, A
Romero, JJ
Hernando, A
González, JM
JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2005, 290 : 1234 - 1236
[5] Crystal structure and magnetic properties of SmCo-based films deposited on hot Si (100) substrates
Li, Yuanxun
Peng, Long
JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2011, 323 (05) : 475 - 478
[6] Magnetic anisotropy in bulk nanocrystalline SmCo5 permanent magnet prepared by hot deformation
Yue, M.
Zuo, J. H.
Liu, W. Q.
Lv, W. C.
Zhang, D. T.
Zhang, J. X.
Guo, Z. H.
Li, W.
JOURNAL OF APPLIED PHYSICS, 2011, 109 (07)
[7] Analysis of crystallization kinetics of sputtered SmCo based permanent magnetic films
Peng, Long
Li, Lezhong
Yang, Dingyu
Zhu, Xinghua
JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2012, 324 (08) : 1539 - 1542
[8] High-coercivity SmCo5 thin films deposited on glass substrates
Zhang, L.N.
Chen, J.S.
Ding, J.
Hu, J.F.
Journal of Applied Physics, 2008, 103 (11):
[9] High-coercivity SmCo5 thin films deposited on glass substrates
Zhang, L. N.
Chen, J. S.
Ding, J.
Hu, J. F.
JOURNAL OF APPLIED PHYSICS, 2008, 103 (11)
[10] Magnetic properties of SmCo-based permanent magnetic films during 25 to 300 °C
Peng Long
Tu Xiaoqiang
Li Lezhong
Wang Rui
JOURNAL OF RARE EARTHS, 2013, 31 (10) : 988 - 991

← 1 2 3 4 5 →