Effect of different shot peening intensities on fatigue resistance of TC17 titanium alloy

被引：0
|
作者：
Bu J. [1 ]
Lü Y. [1 ]
Liu B. [1 ]
Han Z. [1 ]
Tong W. [1 ]
Gao Z. [1 ]
机构：
[1] Shenyang Engine Research Institute, Aero Engine Corporation of China, Shenyang
来源：
Hangkong Dongli Xuebao/Journal of Aerospace Power | 2022年 / 37卷 / 06期
关键词：
delaminating; fatigue life; microcrack; residual compressive stress; shot peening intensity; TC17 titanium alloy;
D O I：
10.13224/j.cnki.jasp.20210257
中图分类号：
学科分类号：
摘要：
In order to improve the fatigue resistance of the TC17 titanium alloy，shot peening on the surface was carried out. The effects of different shot peening intensities on fatigue resistance of TC17 titanium alloy were studied by means of rotary bending fatigue test，fracture analysis，residual stress field analysis，microstructure observation and surface integrity analysis before and after shot peening. The results showed that surface roughness of titanium alloy was increased from 0. 315 μm to 0. 5-1. 0 μm after shot peening. Severe plastic deformation occurred on the surface during shot peening and the surface grains were refined. Residual compressive stress was introduced into the surface，the layer depth of residual compressive stress was about 125-151 μm，and the maximum compressive stress appeared about 30 μm in depth from the surface. The fatigue life of the rotary bending sample after 0. 3 mm • N shot peening was better than that of other samples. Under the stress levels of 740 MPa and 840 MPa， the fatigue life of 0. 3 mm • N shot peened sample increased by 4. 5 times and 7. 5 times than that of non - shot peened sample， respectively. The increase of fatigue life was attributed to the inhibition of fatigue crack initiation and propagation by the refined grains， high - density dislocations and residual compressive stress on the surface induced by shot peening. Excessive shot peening intensity caused the high surface roughness， delamination and microcrack formation on the surface， which resulted in the decrease of fatigue life of 0. 35 mm • N and 0. 4 mm • N shot peened samples. © 2022 BUAA Press. All rights reserved.
引用
收藏
页码：1225 / 1233
页数：8
相关论文
共 21 条
  • [1] SHI Lei, YANG Guang, LIN Wenjun, Influence mechanism of leading - edge erosion on aerodynamic performance of fan rotor blade, Acta Aeronautica et Astronautica Sinica, 40, 10, (2019)
  • [2] CHEN Yunyong, YANG Xiaohe, WEI Feifei, Development trend of high bypass ratio turbofans design technology[J], Acta Aeronautica et Astronautica Sinica, 38, 9, (2017)
  • [3] ZHU Qichen, CHEN Yong, XIAO Jiaguangyi, Study on laminate design method of composite fan blade, Aeroengine, 44, 3, pp. 49-54, (2018)
  • [4] YANG Ruiyao, The fatigue life calculation and vibration characteristic analysis on fan blades of aircraft engine, (2016)
  • [5] DONG Yi, LI Wei, ZHOU Yangyang, Et al., The thermal compression deformation behavior of TC17 titanium alloy[J], World Nonferrous Metals, 8, pp. 22-26, (2020)
  • [6] BU Jiali, GAO Zhikun, TONG Wenwei, Et al., Crack failure analysis of a fan rotor blade, Aeroengine, 45, 1, pp. 12-16, (2019)
  • [7] YU Bingbing, CHEN Zhiyong, ZHAO Zibo, Et al., Microstructure and Mechanical properties of electron beam weld-ment of titanium alloy TC17[J], Acta Metallurgica Sinica, 52, 7, pp. 831-841, (2016)
  • [8] JIN Junlong, WAN Xiaohui, GUO Delun, Microstructure and mechanical properties of welded joint of TC17 titanium alloy[J], Aeronautical Manufacturing Technology, 60, 10, pp. 79-81, (2017)
  • [9] LI Di, CHEN Yunyong, LIAO Lianfang, Experimental design and verification of hollow fan blade high cycle fatigue [J], Journal of Aerospace Power, 32, 6, pp. 1359-1365, (2017)
  • [10] WANG Zhonglin, CHEN Yong, OUYANG Hua, Et al., Vibration characteristics of titanium wide - chord fan blade, Journal of Aerospace Power, 33, 11, pp. 2593-2601, (2018)
123