INFLUENCE OF COMBINED CHEMICAL-THERMAL TREATMENT MODES ON STRUCTURE FORMATION OF HIGH-SPEED STEEL

被引：0
|
作者：
Mukhammadjonovich B.J. [1 ]
Kizi P.M.M. [2 ]
Ugli E.M.S. [1 ]
机构：
[1] Mechanical Engineering Technologies Department, Belarusian-Uzbek Intersectoral Institute of Applied Technical Qualifications, Tashkent
[2] Kimyo International University, Tashkent
来源：
Int. J. Mech. Appl. Mech. | / 14卷 / 95-100期
关键词：
Hardening; High-speed steel; Microhardness; Nitro-carburization; Retained austenite; Tempering;
D O I：
10.17683/ijomam/issue14.12
中图分类号：
学科分类号：
摘要：
The paper presents the results of studies on the structure formation of R6M5 steel during heat treatment, which consists of hardening steel from generally accepted temperatures, and carrying out the process of low-temperature nitro-carburization combined with the tempering process. It has been established that the size of the austenite grain depends on the holding time when heating the steel for hardening, and the amount of retained austenite sharply decreases at a temperature of 550 °C and a holding time of 2.5 hours. © 2023, Cefin Publishing House. All rights reserved.
引用
收藏
页码：95 / 100
页数：5
相关论文
共 50 条
  • [1] Promotion of steel corrosion resistance by chemical-thermal treatment in electrolytes
    Parshutin, V. V.
    Pasinkovskii, E. A.
    SURFACE ENGINEERING AND APPLIED ELECTROCHEMISTRY, 2007, 43 (06) : 431 - 433
  • [2] Modification of structure and mechanical properties of high-speed steel P18 at combined plasma and thermal treatment
    Cherenda, N. N.
    Uglov, V. V.
    Bibik, N. V.
    Gusakova, S. V.
    Astashinskii, V. M.
    Kuzmitskii, A. M.
    Ukhov, V. A.
    JOURNAL OF SURFACE INVESTIGATION, 2011, 5 (02): : 305 - 309
  • [3] Modification of structure and mechanical properties of high-speed steel P18 at combined plasma and thermal treatment
    N. N. Cherenda
    V. V. Uglov
    N. V. Bibik
    S. V. Gusakova
    V. M. Astashinskii
    A. M. Kuzmitskii
    V. A. Ukhov
    Journal of Surface Investigation. X-ray, Synchrotron and Neutron Techniques, 2011, 5 : 305 - 309
  • [4] THE PROPERTIES OF HIGH-SPEED STEEL Р6М5, DEPENDING ON THE COMBINED CHEMICAL HEAT TREATMENT
    Begatov J.
    Ahmadjonovich S.B.
    Yakubova M.
    Kuchkarova D.
    Djalilova M.
    International Journal of Mechatronics and Applied Mechanics, 2022, 2022 (11): : 119 - 122
  • [5] Promotion of steel corrosion resistance by chemical-thermal treatment in electrolytes
    V. V. Parshutin
    E. A. Pasinkovskii
    Surface Engineering and Applied Electrochemistry, 2007, 43 (6) : 431 - 433
  • [6] Influence of thermocyclic treatment on structure and properties of high-speed steel of electroslag remelting
    Gulichandanov, E.L.
    Chajdorov, A.D.
    2002, Mashinostroeni
  • [7] COMBINED INFLUENCE OF ZIRCONIUM AND CALCIUM ON PROPERTIES OF HIGH-SPEED STEEL
    KHARCHENKO, VA
    SLYUSAREV, VY
    KOCHERGIN, VG
    ALEKSEICHUK, IS
    RUSSIAN METALLURGY, 1985, (04): : 104 - 107
  • [8] Modification of the structure and properties of high-speed steel by combined vacuum-plasma treatment
    Grigoriev, S. N.
    Metel', A. S.
    Fedorov, S. V.
    METAL SCIENCE AND HEAT TREATMENT, 2012, 54 (1-2) : 8 - 12
  • [9] Modification of the structure and properties of high-speed steel by combined vacuum-plasma treatment
    S. N. Grigoriev
    A. S. Metel’
    S. V. Fedorov
    Metal Science and Heat Treatment, 2012, 54 : 8 - 12
  • [10] Combined bulk-plasma treatment of the high-speed steel
    Samotugin, S.S.
    Nesterov, O.Yu.
    Fizika i Khimiya Obrabotki Materialov, 2002, (05): : 14 - 17
12345