High temperature oxidation behavior of pure Zr coated by microarc oxidation in 1000~1200 °C steam

被引：0
|
作者：
Wang X.-P. [1 ,2 ,3 ]
Liao Y.-Z. [1 ,2 ]
Guan H.-H. [1 ,2 ]
Gao C.-L. [1 ,2 ]
Zhu M.-H. [1 ,2 ]
Jin X.-Y. [2 ]
Xu C. [1 ,2 ]
Du J.-C. [1 ,2 ]
Xue W.-B. [1 ,2 ,3 ]
机构：
[1] Key Laboratory of Beam Technology of Ministry of Education, College of Nuclear Science and Technology, Beijing Normal University, Beijing
[2] Beijing Radiation Center, Beijing
[3] Innovation Center of Nuclear Materials for National Defense Industry, Beijing
来源：
Surface Technology | 2021年 / 50卷 / 06期
基金：
中国国家自然科学基金;
关键词：
High-temperature steam oxidation; Hydrogen pickup; Microarc oxidation; Oxidation kinetics; Pure zirconium;
D O I：
10.16490/j.cnki.issn.1001-3660.2021.06.002
中图分类号：
学科分类号：
摘要：
The work aimed to study the effect of microarc oxidation (MAO) surface treatment on the high temperature steam oxidation behavior of pure zirconium. The oxidation resistance of pure Zr with and without a MAO ceramic coating of about 2.5 µm thick in 1000~1200 °C steam environment was evaluated by a thermogravimetric analyzer (TGA). The microstructures and phase components of bare and MAO-coated Zr before and after steam oxidation were analyzed. Their composition depth profiles of Zr, O, P, Na, C, and H elements before and after steam oxidation test were carried out by glow discharge optical emission spectroscopy (GDOES). It was found that their kinetic transition temperature for accelerated oxidation was about 600 °C in water vapor environment. The mass gain of MAO-coated pure Zr was lower than that of bare Zr after 3600 s steam oxidation at 1000 °C, however, their oxidation kinetics curves almost overlapped at 1100 °C and 1200 °C. In the initial stage of steam oxidation, oxygen atoms diffused rapidly into Β-Zr substrate. When the thick α-Zr(O) layer and ZrO2 layer were formed, the oxidation rate of bare and MAO-coated Zr was mainly governed by the oxygen diffusion rate in α-Zr(O) layer. Furthermore, the zirconia layer prevented from hydrogen pickup into Zr substrate. After high temperature steam oxidation, the oxide layers of both bare and MAO coated pure Zr consisted of monoclinic zirconia (M-ZrO2) and a little tetragonal zirconia (T-ZrO2) phases. The MAO coating enhanced the steam oxidation resistance of pure Zr below 1000 °C, but not above 1100 °C. © 2021, Chongqing Wujiu Periodicals Press. All rights reserved.
引用
收藏
页码：23 / 31
页数：8
相关论文
共 53 条
  • [1] Yerokhin A.L., Nie X., Leyland A., Et al., Plasma electrolysis for surface engineering[J], Surface & coatings technology, 122, 2-3, pp. 73-93, (1999)
  • [2] Wei K., Xue W., Qu Y., Et al., Advance in microarc oxidation surface treatment on Zr[J], Surface technology, 48, 7, pp. 11-23, (2019)
  • [3] Zou Z., Xue W., Jia X., Et al., Effect of voltage on properties of microarc oxidation films prepared in phosphate electrolyte on Zr-1Nb alloy[J], Surface & coatings technology, 222, pp. 62-67, (2013)
  • [4] Sowa M., Simk W., Effect of DC plasma electrolytic oxidation on surface characteristics and corrosion resistance of zirconium[J], Materials, 11, 5, (2018)
  • [5] Cheng Y., Matykina E., Skeldon P., Et al., Characterization of plasma electrolytic oxidation coatings on zircaloy-4 formed in different electrolytes with AC current regime[J], Electrochimica acta, 56, 24, pp. 8467-8476, (2011)
  • [6] Farrakhov R.G., Mukaeva V.R., Fatkullin A.R., Et al., Plasma electrolytic oxidation treatment mode influence on corrosion properties of coatings obtained on Zr-1Nb alloy in silicate-phosphate electrolyte[J], IOP conference series: Materials science and engineering, 292, 1, (2018)
  • [7] Xue W., Zhu Q., Jin Q., Et al., Characterization of ceramic coatings fabricated on zirconium alloy by plasma electrolytic oxidation in silicate electrolyte[J], Materials chemistry and physics, 120, 2-3, pp. 656-660, (2010)
  • [8] Wang L., Hu X., Nie X., Deposition and properties of zirconia coatings on a zirconium alloy produced by pulsed DC plasma electrolytic oxidation[J], Surface & coatings technology, 221, pp. 150-157, (2013)
  • [9] Wang Y., Tang H., Wang R., Et al., Cathodic voltagedependent composition, microstructure and corrosion resistance of plasma electrolytic oxidation coatings formed on Zr-4 alloy[J], RSC advances, 6, 41, pp. 34616-34624, (2016)
  • [10] Lai P., Zhang H., Zhang L., Et al., Effect of micro-arc oxidation on fretting wear behavior of zirconium alloy exposed to high temperature water[J], Wear, 424-425, pp. 53-61, (2019)
123456