Study on the Preparation and Properties of Phase Change Cloud Concrete Stone Cementitous Composites

被引：0

作者：

Zhang D. ^{[1
]}

Liang W. ^{[1
]}

Yang C. ^{[1
,2
]}

Chen J. ^{[1
]}

Li M. ^{[2
]}

Xu F. ^{[1
]}

Xu L. ^{[1
]}

机构：

[1] College of Civil Engineering and Mechanics, Xiangtan University, Hunan, Xiangtan

[2] School of Civil Engineering, Southeast University, Nanjing

来源：

Cailiao Daobao/Materials Reports | 2023年 / 37卷 / 23期

基金：

中国国家自然科学基金;

关键词：

composite phase change aggregate; encapsulation; mechanical property; phase change concrete; phase change paraffin; thermal performance;

D O I：

10.11896/cldb.22060207

中图分类号：

学科分类号：

摘要：

The phase-change cloud concrete stone (CCS) aggregate and phase-change CCS concrete were prepared by vacuum adsorption to improve the paraffin adsorption rate of CCS, which used paraffin as the phase change material (PCM) and CCS as the adsorption matrix. Then the epoxy resin and cement powder were combined to encapsulate them, and their mechanical and thermal properties were studied. The results revealed that vacuum adsorption can significantly improve the paraffin adsorption rate of phase-change CCS aggregates, and the composite encapsulation of epoxy resin and cement powder can reduce the paraffin leakage rate to below 0.2%. With the increase of phase change aggregate content, the mechanical properties of phase-change CCS concrete gradually decrease, but its heat storage and release effect gradually enhanced. The compressive strength of the phase change CCS concrete was 30.9 MPa when the mixture is 50%, which was 15.8% smaller than that of normal CCS concrete (36.7 MPa), and the splitting tensile strength was 3.2 MPa, which was 30.4% lower than that of normal CCS concrete (4.6 MPa). The heat storage performance of the phase-change CCS concrete is excellent. Its strength shows an increasing trend after 150 phase-change cycles, meeting the basic requirements of LC30 concrete. © 2023 Cailiao Daobaoshe/ Materials Review. All rights reserved.

引用

共 16 条

[1] Ostry M, Bantova S, Struhala K., Molecules, 25, 12, (2020)
[2] Bentz D P, Turpin R., Cement and Concrete Composites, 29, 7, (2007)
[3] Li J, Zhang J, Fu M Q., Materials Reports, 35, (2021)
[4] Ahmet S, Tawfik A S, G觟khan H, Et al., Journal of Molecular Liquids, 328, (2021)
[5] Li L., Preparation and properties of phase change materials and energy storage concrete
[6] Wang X, Fang J H, Wu Jiang, New Chemical Materials, 47, 9, (2019)
[7] Zhou J T, Nie Z X, Guo Z W, Et al., Journal of Jiangsu University(Natural Science Edition), 41, 5, (2020)
[8] Tian Y, Lai Y M, Pei W S, Et al., Construction and Building Materials, 127, 329, (2022)
[9] Zhao S X, Yan H, Wang H T., Materials Reports, 31, 10, (2017)
[10] Zhu J Q, Li J L, Zhou W B., Energy Storage Science and Technology, 6, 2, (2017)

← 1 2 →