Research progress of corrosion and wear resistance coatings in marine engineering environment

被引：2
|
作者：
Cui H.-Z. [1 ,2 ]
Lian X.-J. [2 ]
机构：
[1] School of Materials Science and Engineering, Ocean University of China, Qingdao
[2] School of Materials Science and Engineering, Shandong University of Science and Technology, Qingdao
来源：
Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals | 2023年 / 33卷 / 04期
基金：
中国国家自然科学基金;
关键词：
abrasion; coating; corrosion; marine environment; test evaluation;
D O I：
10.11817/j.ysxb.1004.0609.2022-43019
中图分类号：
学科分类号：
摘要：
The key parts of marine equipment are exposed in a complex environment of corrosion-wear interaction, which suffers serious surface abrasion, and affects the reliability and safety. One effective way to solve this challenge is to reinforce the surface of the workpiece to form a protective coating. In this paper, the research progress of wear and corrosion resistant coatings in marine environment in recent years were reviewed, including materials and preparation technology, mechanical-electrical coupling damage mechanism, damage evaluation methods, and the application of new methods such as high-throughput technology. The development trend of coating structure and properties regulation, residual stress modification and service life extension were summarized, and the future development direction of marine corrosion and wear resistance technology was forecasted. © 2023 Central South University of Technology. All rights reserved.
引用
收藏
页码：1179 / 1208
页数：29
相关论文
共 169 条
  • [1] LI Fang-po, LIU Yong-gang, WANG Xin-hu, Analysis of manufacturing factors affecting drilling string failure, Drilling & Production Technology, 36, 6, (2013)
  • [2] LIU Gu-feng, WANG Rong, LUO She-ji, The torsion fatigue life of the S135 drill pipe steel and its breaking property, China Petroleum Machinery, 39, 4, pp. 4-6, (2011)
  • [3] LI F P, LIU Y G, WANG X H, Et al., Failure analysis of d 127 mm IEU G105 drill pipe wash out[J], Engineering Failure Analysis, 18, 7, (2011)
  • [4] MORCILLO M, CHICO B, DIAZ I, Et al., Atmospheric corrosion data of weathering steels: A review[J], Corrosion Science, 77, (2013)
  • [5] LI Xiao-gang, Corrosion resistant low alloy structural steels, (2018)
  • [6] WU W, LIU Z Y, WANG Q Y, Et al., Improving the resistance of high-strength steel to SCC in a SO<sub>2</sub>-polluted marine atmosphere through Nb and Sb microalloying, Corrosion Science, 170, (2020)
  • [7] LIU C, JIANG Z H, ZHAO J B, Et al., Influence of rare earth metals on mechanisms of localised corrosion induced by inclusions in Zr-Ti deoxidised low alloy steel, Corrosion Science, 166, (2020)
  • [8] SUNDARESAN C, RAJASEKARAN B, VARALAKSHMI S, Et al., Comparative hot corrosion performance of APS and Detonation sprayed CoCrAlY, NiCoCrAlY and NiCr coatings on T91 boiler steel, Corrosion Science, 189, (2021)
  • [9] MAZAHERI T H, SHOJA-RAZAVI R, ERFANMANESH M, Et al., Evaluation of the mechanical properties of WC-Ni composite coating on an AISI 321 steel substrate, Optics & Laser Technology, 127, (2020)
  • [10] ZHAO G P, YUAN Y H, ZHANG P, Et al., Influence of orientations biomimetic units processed by laser on wear resistance of 6082 aluminium alloy, Optics & Laser Technology, 127, (2020)
12345678910