Investigation on high speed laser-MIG hybrid welding process of 6N01S-T5 aluminum alloy

被引：0
|
作者：
Wang W. [1 ]
Wang H. [1 ]
Chen H. [1 ]
Zhu Z. [1 ]
机构：
[1] Southwest Jiaotong University, Chengdu
来源：
Hanjie Xuebao/Transactions of the China Welding Institution | 2019年 / 40卷 / 07期
关键词：
6N01S-T5 aluminum alloy; High speed welding; Laser-MIG hybrid welding; Residual stress; Welding distortion;
D O I：
10.12073/j.hjxb.2019400181
中图分类号：
学科分类号：
摘要：
To reduce the welding distortion and joint softening defects of 6N01S-T5 aluminum alloy, high-speed (4.8 m/min) laser-MIG hybrid welding process is performed. The mechanical properties and microstructure of welded joints are analyzed by microhardness test, tensile test, metallographic and SEM with EDS. The welding distortion of the butt joint is tested by coordinate measuring apparatus. The residual stress is measured by X-ray residual stress measurement instrument. The results show that the good appearance of weld is attained at the welding speed of 4.8 m/min. The average tensile strength of the high speed welding joint is 207 MPa, which is 71% of the base metal. Compared with the low speed welding process, the welding wire consumption is reduced by 68% and the welding efficiency is greatly improved at high speed welding process. Meanwhile, the width of the joint softening zone is reduced by 60%. The welding distortion is smaller and the range of residual tensile stress is narrower. © 2019, Editorial Board of Transactions of the China Welding Institution, Magazine Agency Welding. All right reserved.
引用
收藏
页码：55 / 60and66
页数：6011
相关论文
共 8 条
  • [1] Yang S., Lin Q., Microstructures and mechanical properties of A6N01 aluminum alloy welding joint, The Chinese Journal of Nonferrous Metals, 22, 10, pp. 2720-2725, (2012)
  • [2] Wu M., Sui X., Yun Z., Et al., Effect of heat aging on performance uniformity of 6N01 aluminum alloy profiles, Nonferrous Metals Engineering, 6, 3, pp. 17-20, (2016)
  • [3] Lou X., Chen M., Wu C., Et al., Humping and undercutting suppression mechanism for high speed TIG-MIG hybrid welding, Transactions of the China Welding Institution, 35, 8, pp. 87-90, (2014)
  • [4] Li X., Wang X., Lei Z., Et al., Investigation on softening of welded joint of side walls of high speed train of 6N01 aluminum alloy, Transactions of the China Welding Institution, 36, 6, pp. 95-98, (2015)
  • [5] Fang X., Wang R., Wang X., Et al., Laser-Mig hybrid welding of 6N01 aluminum alloy profile for high speed train, Welding & Joining, 2, pp. 54-58, (2015)
  • [6] Casalino G., Mortello M., Leo P., Et al., Study on arc and laser powers in the hybrid welding of AA5754 Al-alloy, Materials & Design, 61, pp. 191-198, (2014)
  • [7] Wang Q., Chen H., Qiu P., Et al., Residual stress and fatigue strength of hybrid laser-MIG-welded A7N01P-T4, Metallurgical and Materials Transactions B, 48, 1, pp. 591-601, (2017)
  • [8] Zhang H., Jin X., Chen G., Et al., Study on the burning loss of magnesium element in fiber laser welding aluminum alloy 5052, Laser Technology, 36, 6, pp. 713-718, (2012)
1