Preparation and ablative mechanism of C/C-ZrC-SiC composites filled with Fe-based superalloy coating

被引：0
|
作者：
Tian T. [1 ]
Sun W. [1 ]
Xiong X. [1 ]
Xu Y. [1 ]
Zhan Z. [1 ]
Chen Z. [1 ]
机构：
[1] Powder Metallurgy Institute, Central South University, Changsha
来源：
Fuhe Cailiao Xuebao/Acta Materiae Compositae Sinica | 2019年 / 36卷 / 07期
关键词：
Ablation; C/C-ZrC-SiC composites; Composite oxides; Fe-based superalloy coating; Low pressure suspension impregnation;
D O I：
10.13801/j.cnki.fhclxb.20181112.002
中图分类号：
学科分类号：
摘要：
The C/C-ZrC-SiC composites filled with Fe-based superalloy coating were prepared by low pressure suspension impregnation to improve the C/C-ZrC-SiC composites used in the field of hypersonic flight vehicle's thermal protective performance. The evolution rule of the surface microstructure of the C/C-ZrC-SiC composites filled with Fe-based superalloy before and after oxy-acetylene flame ablation was studied by means of XRD, SEM and EDS. And the effect of the Fe-based superalloy coating on the ablation behavior of the C/C-ZrC-SiC composites was clarified. The results show that the C/C-ZrC-SiC composites are infiltrated by low pressure suspension infiltration at 1 650℃ for 2 h, and a uniform, dense and tightly bonded Fe-based superalloy coating is formed on the surface. After the ablation at 2 500℃ for 180 s, the surface of the modified the C/C-ZrC-SiC composites generates a smaller ablation pit, and the mass and linear ablation rate are reduced by 8% and 35% respectively than the unmodified sample. And a uniform and dense protective layer of the Fe2O3-ZrO2 composite oxides is formed on the surface, which greatly reduces the occurrence of surface cracks, holes and other defects, thereby reducing the diffusion rate of oxygen and the stress concentration caused by defects. The Fe-based superalloy coating improves the high temperature oxidation resistance and mechanical corrosion resistance of the C/C-ZrC-SiC composites. © 2019, Editorial Office of Acta Materiae Compositae Sinica. All right reserved.
引用
收藏
页码：1691 / 1699
页数：8
相关论文
共 30 条
  • [1] Xie F.Y., Li G., Xu Z.C., The concept and development of hypersonic aircraft, Aerodynamic Missile Journal, 5, pp. 27-31, (2004)
  • [2] Jiang P., Kuang Y., Xie X.P., Et al., Research status and development trend of hypersonic flight vehicles in abroad, Aerodynamic Missile Journal, 7, pp. 19-24, (2007)
  • [3] Lu Q., Hu L.F., Luo X.G., Et al., Development of ceramic composite and hot structures for hypersonic vehicles, Journal of the Chinese Ceramic Society, 41, 2, pp. 251-260, (2013)
  • [4] Liu J., Liu W.Q., Wang Q., Applications of C/C composite materials in hypersonic aircraft, Aerodynamic Missile Journal, 5, pp. 77-79, (2013)
  • [5] Zeng Y., Zhang W.Z., Xiong X., Anti-oxidation mechanisms of the SiC/ZrB<sub>2</sub>-MoSi<sub>2</sub> coating on the carbon/carbon composites, Acta Materiae Compositae Sinica, 27, 3, pp. 50-55, (2010)
  • [6] Bai H.D., Zhang H., Ye Y.C., Preparation and property of C<sub>f</sub>/HfC composites by liquid impregnation combined reactive melt infiltration, Acta Materiae Compositae Sinica, 33, 6, pp. 1259-1265, (2016)
  • [7] Zhang Q., Cui H., Zhu Y., Et al., Preparation and properties of ZrB<sub>2</sub>-SiC compound ceramic coating for C/C-SiC composites, Acta Materae Compositae Sinica, 35, 3, pp. 640-646, (2018)
  • [8] Wang S.L., Li H., Ren M.S., Et al., Favrication and ablation performances of ZrC-SiC-C/C composites, Acta Materiae Compositae Sinica, 34, 5, pp. 1040-1047, (2017)
  • [9] Zhou L., Zhou Y.H., Developments of nonablative thermal materials in hypersonic aircraft, Aerodynamic Missile Journal, 1, pp. 14-24, (2018)
  • [10] Chen S.A., Zhang C.R., Zhang Y.D., Et al., Mechanism of ablation of 3D C/ZrC-SiC composite under an oxyacetylene flame, Corrosion Science, 68, 11, pp. 168-175, (2013)
123