Forming Characteristics of Nano-Precipitation Strengthened Cold-Rolled Batch Annealed HSLA Sheet Steels (>490MPa Yield Strength)

被引：0

作者：

Biswas S. ^{[1
]}

Chen B. ^{[1
]}

Bhartiya S. ^{[1
]}

Injeti Y. ^{[1
]}

Williams W. ^{[1
]}

De A. ^{[1
]}

机构：

[1] Big River Steel, United States

来源：

SAE International Journal of Advances and Current Practices in Mobility | 2023年 / 6卷 / 02期

关键词：

Compendex;

D O I：

10.4271/2023-01-0612

中图分类号：

学科分类号：

摘要：

A low carbon Ti-microalloyed chemistry was selected for the development of family of cold-rolled and batch-annealed high-strength high-formable steels through EAF-LMF-CSP route. A clean steel practice combined with a suitable choice of hot rolling and batch annealing practice were optimized to retain precipitate strengthening in the final fully processed steel and microstructural attributes that resulted in superior forming characteristics. The enhanced balance of strength and formability (hole expansion ratio values of 70-100% for thicknesses of 0.80-1.20 mm and tensile strength ranging from 571-709 MPa) attributed to the optimization of the microstructure through controlled recrystallization and grain growth. In this article, production strategy and formability characterization of high-strength low-alloy steels with minimum yield strength of 490 MPa will be discussed, and results will be presented. © 2023 SAE International. All Rights Reserved.

引用

页码：586 / 592

页数：6

共 9 条

[1] DEVELOPMENT OF CONTINUOUSLY ANNEALED HIGH-STRENGTH COLD-ROLLED SHEET STEELS
ARAKI, K
FUKUNAKA, S
UCHIDA, K
TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1977, 17 (12) : 701 - 709
[2] Cold-rolled, 980MPa grade sheet steels with excellent elongation and λ-value characteristics
Miura, Masaaki
Nakaya, Michiharu
Mukai, Youichi
R and D: Research and Development Kobe Steel Engineering Reports, 2007, 57 (02): : 15 - 18
[3] Precipitation and texture formation in two cold rolled and batch annealed interstitial-free high strength steels
Ghosh, P.
Ray, R. K.
Bhattacharya, B.
Bhargava, S.
SCRIPTA MATERIALIA, 2006, 55 (03) : 271 - 274
[4] Comparative study of precipitation behavior and texture formation in cold rolled-batch annealed and cold rolled-continuous annealed interstitial free high strength steels
Ghosh, P.
Bhattacharya, B.
Ray, R. K.
SCRIPTA MATERIALIA, 2007, 56 (08) : 657 - 660
[5] Study of the Effect of Microstructure Characteristics on Corrosion Resistance of Cold-Rolled Micro-Alloyed Sheet Steels (Hsla) of Strength Classes 340–420 for Automobile Building
I. G. Rodionova
A. V. Amezhnov
D. L. D’yakonov
N. G. Shaposhnikov
O. N. Baklanova
Yu. S. Gladchenkova
Metallurgist, 2020, 63 : 1165 - 1177
[6] Study of the Effect of Microstructure Characteristics on Corrosion Resistance of Cold-Rolled Micro-Alloyed Sheet Steels (Hsla) of Strength Classes 340-420 for Automobile Building
Rodionova, I. G.
Amezhnov, A. V.
D'yakonov, D. L.
Shaposhnikov, N. G.
Baklanova, O. N.
Gladchenkova, Yu. S.
METALLURGIST, 2020, 63 (11-12) : 1165 - 1177
[7] PROCESSING TECHNIQUES AND FORMABILITY OF AGE-HARDENABLE, LOW YIELD, HIGH-TENSILE STRENGTH COLD-ROLLED SHEET STEELS
OHASHI, N
TAKAHASHI, I
HASHIGUCHI, K
TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1978, 18 (06) : 321 - 329
[8] Features of the Effect of Microstructure Characteristics on Corrosion Resistance of Cold-Rolled High-Strength Low-Alloy Steels (HSLA) Grade 260–300 for Automobile Building
I. G. Rodionova
A. V. Amezhnov
N. G. Shaposhnikov
Y. S. Gladchenkova
D. L. D’yakonov
Metallurgist, 2020, 63 : 920 - 932
[9] Features of the Effect of Microstructure Characteristics on Corrosion Resistance of Cold-Rolled High-Strength Low-Alloy Steels (HSLA) Grade 260-300 for Automobile Building
Rodionova, I. G.
Amezhnov, A. V.
Shaposhnikov, N. G.
Gladchenkova, Y. S.
D'yakonov, D. L.
METALLURGIST, 2020, 63 (9-10) : 920 - 932

← 1 →