Fabrication and characterization of biodegradable hydrogel beads of guar gum for the removal of chlorpyrifos pesticide from water

A new guar gum hydrogel beads were fabricated by dropping method from an aqueous solution of guar gum (GG) using ammonium persulphate and polyethylene glycol as initiator and crosslinker respectively, for the adsorption of chlorpyrifos (CP) from water. The semi-crystalline nature of the synthesized beads was confirmed by FESEM analysis. The TGA studies implied that the beads were thermally stable up to 600 degrees C. The maximum swelling ratio of 1400 gg- 1 was attained at pH 9.2 and 80 min. The evidence of a strong absorption band was found in FTIR spectrum at 584 cm- 1 due to -P=S of the adsorbed pesticide CP. The maximum adsorption of CP was found to be 220.97 mgg-1. The adsorption followed pseudo second-order kinetics and Langmuir adsorption isotherm with regression coefficients 0.9998 and 0.9938 which followed the chemisorption process. It is due to the hydrolysis of CP at pH 9.2 to yield 3,5,6-trichloropyridinol which in turn reacts with the carboxylic group present in GG giving -N-C=O linkage. A -Delta G indicates that the process is spontaneous and involves chemisorption which is thermodynamically and kinetically favorable and a -Delta H value (-10.37 kJ/mol) suggests that the adsorption is exothermic.