Microstructure and properties of Ni20Cr-MoS2 composite coating by subsonic flame spraying

被引：1

作者：

Yang, Kenan ^{[1
,2
]}

Li, Haixin ^{[1
]}

Wei, Min ^{[2
]}

Song, Zhanyong ^{[3
]}

Li, Xuefeng ^{[1
]}

Yu, Chuanyong ^{[2
]}

机构：

[1] Harbin Engn Univ, Yantai Res Inst, Yantai 264006, Peoples R China

[2] Foshan Univ, Sch Mechatron Engn & Automat, Foshan 528225, Peoples R China

[3] Army Acad Armored Forces, Natl Key Lab Remfg, Beijing 100072, Peoples R China

来源：

SURFACE & COATINGS TECHNOLOGY | 2024年 / 489卷

关键词：

Subsonic flame-spraying technology; MoS2; Microstructure; Cohesion strength; Tribological property; TRIBOLOGICAL PROPERTIES; RESISTANCE; MECHANISM; WEAR; EVOLUTION; FRICTION; ADHESION; CONTACT; DAMAGE;

D O I：

10.1016/j.surfcoat.2024.131083

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

In this study, a Ni20Cr-MoS2 composite coating was fabricated using subsonic flame-spraying technology, and the effects of adding MoS2 on the microstructure, mechanical properties, and tribological properties of the coating were studied. The microstructure analysis of the coatings revealed that the Ni20Cr and Ni20Cr-MoS2 coatings prepared by subsonic flame spraying had fewer microscopic defects and significant particle flattening. After the addition of MoS2, the porosity of the coating decreased, whereas its microhardness increased. The cohesive strength of the coating was measured using the scratch method, and it was found to be enhanced after the addition of MoS2. Moreover, in the dry friction state, compared with the Ni20Cr coating, the Ni20Cr-MoS2 coating performs better. At a load of 20 N, the friction and wear performances of the Ni20Cr-MoS2 coating were the best, and the friction coefficient decreased by 11.63 %. Based on this, the relationships between the cohesive strength and tribological properties and between the wear mechanism and scratch mechanism of the coating are discussed.

引用

页数：12

共 50 条

[1] Properties of PA(polyamide) coating and PA/MoS2 composite coatings by flame spraying
Xu, HY
Zhou, HD
Chen, JM
Feng, ZZ
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2004, 14 : 67 - 71
[2] Microstructure and Wear-Resistant Properties of Ni80Al20-MoS2Composite Coating on Sled Track Slippers
Wang, Weihua
Xie, Faqin
Wu, Xiangqing
Zhu, Zheng
Wang, Shaoqing
Lv, Tao
COATINGS, 2020, 10 (07)
[3] Influence of heat treatment on microstructure and tribological properties of flame spraying Fe-Ni-Al alloy coating
Mouadji, Youcef
Bradai, Mohand Amokrane
Younes, Rassim
Sad-eddine, Abdelhamid
Benabbas, Abderrahim
JOURNAL OF CENTRAL SOUTH UNIVERSITY, 2018, 25 (03) : 473 - 481
[4] Microstructure and mechanical properties of TiB2-Ni composite coating
Li, Zhuoxin, 1600, Harbin Research Institute of Welding (35):
[5] Microstructure and properties of plasma clad Ni composite coating
Liu Shenglin
Sun Dongbai
Fan Zishuan
Yu Hongying
Wang Xudong
Meng Huimin
Li Huiqin
RARE METAL MATERIALS AND ENGINEERING, 2006, 35 : 232 - 235
[6] Microstructure and Tribological Properties of PlasmaSprayed Ni/MoS2 Solid Lubrication Coating
Ma Guozheng
稀有金属材料与工程, 2012, 41 (S1) : 331 - 335
[7] Microstructure and mechanical properties of HVOF sprayed nanocrystalline Cr3C2-25(Ni20Cr) coating
Roy, M.
Pauschitz, A.
Bernardi, J.
Koch, T.
Franek, F.
JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2006, 15 (03) : 372 - 381
[8] Microstructure and mechanical properties of HVOF sprayed nanocrystalline Cr3C2-25(Ni20Cr) coating
M. Roy
A. Pauschitz
J. Bernardi
T. Koch
F. Franek
Journal of Thermal Spray Technology, 2006, 15 : 372 - 381
[9] Microstructure and Tribological Properties of WC/Ni-MoS2 Titanium-Based Composite Coating on TC4
Wang, Changhao
Yan, Xiaohui
Zhang, Tiangang
Zhang, Qiyu
Zhang, Zhiqiang
COATINGS, 2024, 14 (09)
[10] Research on the microstructure and space tribology properties of electric-brush plated Ni/MoS2-C composite coating
Ma Guozheng
Xu Binshi
Wang Haidou
Wang Xiaohe
Li Guolu
Zhang Sen
SURFACE & COATINGS TECHNOLOGY, 2013, 221 : 142 - 149

← 1 2 3 4 5 →