Freezing non-radiative recombination in high-performance CsPbBr3 single crystal x-ray detector

Though CsPbBr3 single crystals (SCs) possess intriguing photoelectronic properties for x/gamma-ray detection, the serious ion migration and high thermally activated carrier concentration at room temperature (RT), typically associated with defect states in CsPbBr3 crystals, result in a high dark current and drift of baseline, hindering their potential applications. In this investigation, liquid nitrogen cooling is proposed to freeze deep-level defects in CsPbBr3 SCs, thereby suppressing the ion migrations and decreasing the thermally excited carrier concentration. Utilizing photoluminescence (PL) and time-resolved PL spectra, coupled with theoretical models for photoexcitation and photoemission processes, the freezing of deep-level defects at liquid nitrogen temperature (LNT) is confirmed, which is conducive to decreasing non-radiative recombination. At LNT, the CsPbBr3 SC exhibits a higher resistivity of 4.95 x 1011 Omega cm and a higher mobility-lifetime product of 9.54 x 10(-3) cm(2) V-1, in contrast to the RT values of 3.86 x 10(9 )Omega cm and 3.67 x 10(-3) cm(2 )V(-1), respectively. Furthermore, the x-ray detector at LNT exhibits a high sensitivity of 9309 mu C Gyair(-1) cm(-2) and an impressively low detection limit of 0.054 nGy s(-1), which offers a route for obtaining highly sensitive x-ray detectors for applications including ultra-low dose radiation imaging.