Ultraviolet Grafting of Bismuth Oxide Enhances the Photocatalytic Performance of PVDF Membrane and Improves the Problem of Membrane Fouling

Photocatalytic membranes are crucial in addressing membrane fouling issues. However, the grafting amount of the catalyst on the membrane often becomes a key factor in restricting the membrane's self-cleaning capability. To address the challenge, this manuscript proposes a method for solving membrane fouling, featuring high grafting rates of bismuth oxide (Bi2O3) and acrylic acid (AA), significant contaminant degradation capability, and reusability. A highly photocatalytic self-cleaning microfiltration membrane made of polyvinylidene fluoride bismuth oxide and acrylic acid (PVDF-g-BA) was prepared by attaching nano Bi2O3 and acrylic acid onto the polyvinylidene fluoride membrane through adsorption/deposition and UV grafting polymerization. Compared with pure membranes and pure acrylic grafted membranes (PVDF-g-AA), the modified membrane grafted with 0.5% bismuth oxide not only improves the grafting rate and filtration performance, but also has higher self-cleaning ability. Furthermore, the degradation effect of this membrane on the organic dye methyl violet 2B under visible light irradiation is very significant, with a degradation rate reaching 90% and almost complete degradation after 12 h. Finally, after repeated filtration and photocatalysis, the membrane can still significantly degrade contaminants and can be reused.