Enhancing the thermoelectric properties of PEDOT:PSS films through the incorporation of g-C3N4 nanosheets and carbon nanotubes

Present study focuses on the synthesis of flexible nanocomposite film made of poly(3,4-ethylenedioxythiophene)poly(styrenesulfonate) (PEDOT:PSS), graphitic carbon nitride (g-C3N4) nanosheets, and carbon nanotubes (CNTs) and how the g-C3N4 nanosheets and CNTs affect the thermoelectric properties of PEDOT:PSS. Incorporating 10 wt% of g-C3N4 nanosheets to PEDOT:PSS improved the Seebeck coefficient to 74.3 mu VK-1, similar to 5 times higher than the PEDOT:PSS film. However, this led to a decrease in electrical conductivity, limiting the power factor to 335.4 mu Wm(-1)K(-2). In order to address this, CNTs were added as conductive fillers. The resulting PEDOT:PSS composite, with 10 wt% of g-C3N4 and 10 wt% CNTs, showed a significant power factor of 589.8 mu Wm(-1)K(-2), an electrical conductivity of 810.6 Scm(-1), and a Seebeck coefficient of 84.5 mu VK-1, indicating a substantial improvement in the thermoelectric performance of pristine PEDOT:PSS. The increased Seebeck coefficient in the PEDOT:PSS and g-C3N4 composite is due to reduced carrier concentration and energy filtering at the interfaces. The enhancement in electrical conductivity and the Seebeck coefficient after adding CNTs is attributed to the formation of conductive networks, increased mobility, and energy filtering at the interfaces between PEDOT:PSS and CNTs. The study suggests that combining g-C3N4 nanosheets and CNTs with PEDOT:PSS could enhance the thermoelectric performance of PEDOT:PSS-based materials.