Pressure-induced softening in bulk modulus due to magnetoelastic coupling in Nd2CoFeO6 double perovskite

In the present work, we have investigated the structural response of transition metal double perovskite oxide Nd2CoFeO6 under pressure by XRD and Raman spectroscopic measurements. From XRD data, we have observed a pressure-induced structural transition from the orthorhombic phase to the monoclinic phase at about 14.8 GPa. An anomalous increase in compressibility at a much lower pressure ( similar to 1.1 GPa) is seen where no structural transition occurs. At about the same pressure, a sudden drop in the slope of the Raman shift is observed. Further investigation at low temperatures reveals that the B 1 g Raman mode is strongly affected by magnetic interactions. Additional high-pressure Raman experiments with the application of a magnetic field have indicated that the mentioned anomaly around 1.1 GPa can be explained by a high-spin to low-spin transition of Co3+. (c) 2024 Author(s). All article content, except where otherwise noted, is licensed under a Creative Commons Attribution (CC BY) license(https://creativecommons.org/licenses/by/4.0/).