Binder-free copper manganese sulfide nanoflake arrays electrodeposited on reduced graphene oxide-wrapped nickel foam as an efficient battery-type electrode for asymmetric supercapacitors

In the current study, 2D interconnected copper manganese sulfide (CMS) nanoflake arrays are successfully electrodeposited on nickel foam (NF) and reduced graphene oxide-coated NF (NF/rGO). A pulsed current electrodeposition method is used to prepare a uniform and homogeneous coverage of rGO on NF. By using rGO as a conductive carbon-based template, an ultrathin nanoflake structure of CMS with smaller dimensions and higher electrochemically active surface area (ECSA) is achieved. The results reveal the battery-type behavior of the assynthesized CMS electroactive materials. At a current density of 5 A g- 1 this electrode delivers a significant specific capacity of 667 C g-1 and maintained a considerable proportion of its initial capacity, with a retention value of 83.2 % even after undergoing 3000 charge/discharge cycles. In addition, an asymmetric supercapacitor is fabricated by setting up the synthesized NF/rGO/CMS sample as the positive electrode and activated carbon as the negative electrode. The constructed device not only delivers an impressive energy density of 63.3 Wh kg-1 accompanied by an outstanding power density of 11214.5 W kg- 1, but also exhibits a considerable cycling durability, enduring only a 12 % decline in specific capacitance after 3000 charge/discharge cycles at a current density of 5 A g-1.-1 .