Nitrogen-doped carbon supported iron nanoparticles for mild catalytic hydrocracking of Xilinguole lignite

Cleaving C -O bridged bonds of lignite via catalytic hydrocracking (CHC) is an effective method to produce chemicals and clean fuels. Herein, a nitrogen-doped carbon supported Fe catalyst was developed by using a onepot method for CHC of Xilinguole lignite (XL) and its related model compounds. The doped nitrogen enhanced the interaction between Fe and N species to form Fe -N sites and favored forming smaller Fe/Fe3C nanocrystals, which played a crucial role in CHC performance. Toluene and phenol were produced from CHC of benzyl phenyl ether (BPE) with high yield and selectivity at 250 degrees C over the optimal catalyst with 4% Fe, without hydrogenation products. The Fe-based catalyst activated both H2 and isopropanol to generate hydrogen radicals for cleaving C -O bridged bonds. The CHC of XL under different temperature and time showed that the yields of oil, asphaltene and preasphaltene were obviously promoted under 325 degrees C, 1 MPa, and 6 h, and they had much higher H/C ratio but remarkably lower O/C ratio, resulting in much higher heating values (28.19-36.90 MJ/kg) than XL. Phenols were the major group component with relative content of 53.6 wt% in oil from CHC, and the asphaltene and preasphaltene from CHC had obviously lower molecular weights, which could attributed to depolymerization of C -O bridged bonds in the XL macromolecular structures over the catalyst.