Fabrication of Erbium-Doped Upconversion Nanoparticles and Carbon Quantum Dots for Efficient Perovskite Solar Cells

Upconversion nanoparticles (UCNPs) and carbon quantum dots (CQDs) have emerged as promising candidates for enhancing both the stability and efficiency of perovskite solar cells (PSCs). Their rising prominence is attributed to their dual capabilities: they effectively passivate the surfaces of perovskite-sensitive materials while simultaneously serving as efficient spectrum converters for sunlight. In this work, we synthesized UCNPs doped with erbium ions as down/upconverting ions for ultraviolet (UV) and near-infrared (NIR) light harvesting. Various percentages of the synthesized UCNPs were integrated into the mesoporous layers of PSCs. The best photovoltaic performance was achieved by a PSC device with 30% UCNPs doped in the mesoporous layer, with PCE = 16.22% and a fill factor (FF) of 74%. In addition, the champion PSCs doped with 30% UCNPs were then passivated with carbon quantum dots at different spin coating speeds to improve their photovoltaic performance. When compared to the pristine PSCs, a fabricated PSC device with 30% UCNPs passivated with CQDs at a spin coating speed of 3000 rpm showed improved power conversion efficiency (PCE), from 16.65% to 18.15%; a higher photocurrent, from 20.44 mA/cm2 to 22.25 mA/cm2; and a superior fill factor (FF) of 76%. Furthermore, the PSCs integrated with UCNPs and CQDs showed better stability than the pristine devices. These findings clear the way for the development of effective PSCs for use in renewable energy applications.