Microstructure and mechanical properties of 2205 duplex stainless steel friction stir welding joint

被引：0

作者：

Jia Z. ^{[1
,2
]}

Zhao Y. ^{[2
]}

Dong C. ^{[2
]}

Wang C. ^{[2
]}

Chen H. ^{[2
]}

机构：

[1] School of Materials Science and Engineering, Central South University, Changsha

[2] Guangdong Provincial Key Laboratory of Advanced Welding Technology, Guangdong Welding Institute (China-Ukraine E.O.Paton Institute of Welding), Guangzhou

来源：

Hanjie Xuebao/Transactions of the China Welding Institution | 2019年 / 40卷 / 03期

关键词：

Duplex stainless steel; Friction stir welding; Mechanical properties; Microstructure;

D O I：

10.12073/j.hjxb.2019400079

中图分类号：

学科分类号：

摘要：

The effects of the welding tool rotation speed on the microstructures and mechanical properties of friction stir welding joints of 4 mm thick 2205 duplex stainless steel sheet were studied. The results indicated that when the welding speed is 50 mm/min and the rotation speed is in the range of 600 ~ 800 r/min, the sound welds can be obtained. The grains in the stir zone of the joint were refined by the dynamic recry stallization, and the hardness value in this zone was relatively high. The grains in the heat affected zone were coarsened by the welding heat and the hardness value in this zone was relatively low. The ferrite content of the obtained joints was within the range of 50%-60%, and the ferrite content in the stir zone was increased with the increase of rotation speed. When the rotational speed was 600 r/min, the tensile strength of the joint reached the maximum 824 MPa, which was 97.3% of the base material, and the fracture location was in the heat affected zone. © 2019, Editorial Board of Transactions of the China Welding Institution, Magazine Agency Welding. All right reserved.

引用

页码：97 / 101

页数：4

共 8 条

[1] Wang Z., Han J., Song H., Et al., Comparative analysis for joint performance of duplex stainless steel by different arc welding methods, Transactions of the China Welding Institution, 32, 4, pp. 37-40, (2011)
[2] Urena A., Otero E., Utrilla M.V., Et al., Weldability of a 2205 duplex stainless steel using plasma arc welding, Materials Processing Technology, 182, 1-3, pp. 624-631, (2007)
[3] Saeid T., Abdollah-Zadeh A., Assadi H., Et al., Effect of friction stir welding speed on the microstructure and mechanical properties of a duplex stainless steel, Materials Science and Engineering: A, 496, 1-2, pp. 262-268, (2008)
[4] Gong L., Zhang B., Wang S., Corrosion resistance of duplex stainless steel welded joint, Transactions of the China Welding Institution, 31, 7, pp. 59-62, (2010)
[5] Santos T.F.A., Marinho R.R., Paes M.T.P., Et al., Microstructure evaluation of UNS S32205 duplex stainless steel friction stir welds, Rem: Revista Escola de Minas, 66, 2, pp. 187-191, (2013)
[6] Liu H., Zhou L., Process in friction stir welding of high melting point materials, Transactions of the China Welding Institution, 28, 10, pp. 101-104, (2007)
[7] Sato Y.S., Nelson T.W., Sterling C.J., Et al., Microstructure and mechanical properties of friction stir welded SAF 2507 super duplex stainless steel, Materials Science and Engineering: A, 397, 1-2, pp. 376-384, (2005)
[8] Saeid T., Abdollah-Zadeh A., Shibayanagi T., Et al., EBSD investigation of friction stir welded duplex stainless steel, World Academy of Science, Engineering and Technology, 61, pp. 376-379, (2010)

← 1 →