Influence of the α fraction on 2205 duplex stainless steel corrosion affected by Pseudomonas aeruginosa

被引：0
|
作者：
Zhu, Liyang [1 ,2 ,3 ,4 ]
Wu, Jiajia [1 ,2 ,3 ,5 ]
Zhang, Dun [1 ,2 ,3 ]
Wang, Peng [1 ,2 ,3 ]
Sun, Zhihua [1 ,2 ,3 ,4 ]
Li, Ce [1 ,2 ,3 ,4 ]
Li, Ee [1 ,2 ,3 ]
机构：
[1] Key Laboratory of Marine Environmental Corrosion and Biofouling, Institute of Oceanology, Chinese Academy of Science, Qingdao,266071, China
[2] Open studio for Marine Corrosion and Protection, Qingdao National Laboratory for Marine Science and Technology, Qingdao,266071, China
[3] Center for Ocean Mega-Science, Chinese Academic of Science, Qingdao,266071, China
[4] University of Chinese Academy of Sciences, Beijing,100049, China
[5] Key Laboratory of Marine Materials and Related Technologies, Ningbo Institute of Materials Technology & Engineering, CAS, Ningbo,315201, China
来源：
Corrosion Science | 2021年 / 193卷
基金：
中国国家自然科学基金;
关键词：
Bacteria - Corrosion resistance - Pitting;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Corrosion of 2205 duplex stainless steel with different α fractions affected by Pseudomonas aeruginosa was investigated. It was found that P. aeruginosa accelerated pitting corrosion, and an α fraction of 53.8% gave the best corrosion resistance, which was related to the highest resistance, and fewest defects of passive films, and least biofilms. Pits appeared at phase boundaries or α phase in biotic media, due to the preferential attachment of bacteria at phase boundaries and their expansion towards α phase. P. aeruginosa kept high volta differences between α and γ phases to promote the anodic dissolution of α phase. Data availability statement: The raw/processed data required to reproduce these findings cannot be shared at this time as the data are related to an ongoing study. © 2021 Elsevier Ltd
引用
收藏
相关论文
共 50 条
  • [1] Influence of the a fraction on 2205 duplex stainless steel corrosion affected by Pseudomonas aeruginosa
    Zhu, Liyang
    Wu, Jiajia
    Zhang, Dun
    Wang, Peng
    Sun, Zhihua
    Li, Ce
    Li, Ee
    [J]. CORROSION SCIENCE, 2021, 193
  • [2] Microbiologically Influenced Corrosion of 2205 Duplex Stainless Steel by Marine Pseudomonas aeruginosa
    Zhou Z.
    Zhang H.
    Liu Y.
    Zhao Y.
    [J]. Cailiao Yanjiu Xuebao/Chinese Journal of Materials Research, 2019, 33 (05): : 321 - 330
  • [3] The effects of a phase on localized corrosion of 2205 duplex stainless steel in the presence of Pseudomonas aeruginosa
    Zhu, Liyang
    Wu, Jiajia
    Wang, Peng
    Zhang, Dun
    Li, Ce
    Gao, Yaohua
    Wang, Wenkai
    [J]. CORROSION SCIENCE, 2024, 232
  • [4] Accelerated corrosion of 2205 duplex stainless steel caused by marine aerobic Pseudomonas aeruginosa biofilm
    Xu, Dake
    Xia, Jin
    Zhou, Enze
    Zhang, Dawei
    Li, Huabing
    Yang, Chunguang
    Li, Qi
    Lin, Hai
    Li, Xiaogang
    Yang, Ke
    [J]. BIOELECTROCHEMISTRY, 2017, 113 : 1 - 8
  • [5] Effect of Cu Addition to 2205 Duplex Stainless Steel on the Resistance against Pitting Corrosion by the Pseudomonas aeruginosa Biofilm
    Li, Ping
    Zhao, Yang
    Liu, Yuzhi
    Zhao, Ying
    Xu, Dake
    Yang, Chunguang
    Zhang, Tao
    Gu, Tingyue
    Yang, Ke
    [J]. JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2017, 33 (07) : 723 - 727
  • [6] The difference in preferential corrosion of 2205 duplex stainless steel induced by Pseudomonas aeruginosa between full and alternate immersion
    Zhu, Liyang
    Wu, Jiajia
    Zhang, Dun
    Wang, Peng
    Li, Ce
    Wang, Yu
    Sun, Zhihua
    [J]. CORROSION SCIENCE, 2022, 208
  • [7] Effect of Cu Addition to 2205 Duplex Stainless Steel on the Resistance against Pitting Corrosion by the Pseudomonas aeruginosa Biofilm
    Ping Li
    Yang Zhao
    Yuzhi Liu
    Ying Zhao
    Dake Xu
    Chunguang Yang
    Tao Zhang
    Tingyue Gu
    Ke Yang
    [J]. Journal of Materials Science & Technology, 2017, 33 (07) : 723 - 727
  • [8] Corrosion behavior of 2205 duplex stainless steel
    Platt, JA
    Guzman, A
    Zuccari, A
    Thornburg, DW
    Rhodes, BF
    Oshida, Y
    Moore, BK
    [J]. AMERICAN JOURNAL OF ORTHODONTICS AND DENTOFACIAL ORTHOPEDICS, 1997, 112 (01) : 69 - 79
  • [9] Influence of the filler material on the pitting corrosion in welded duplex stainless steel 2205
    Múnez, C.J.
    Utrilla, M.V.
    Ureña, A.
    Otero, E.
    [J]. Revista de Metalurgia (Madrid), 2007, 43 (04): : 245 - 251
  • [10] Influence of the filler material on pitting corrosion in welded duplex stainless steel 2205
    Múnez C.J.
    Utrilla M.V.
    Ureña A.
    Otero E.
    [J]. Welding International, 2010, 24 (02) : 105 - 110
12345