Characterization of microstructure of hot-dip al-si coating

被引：0
|
作者：
Cui G.-B. [1 ]
Ju X.-H. [1 ]
Yin L.-X. [1 ]
Yan C.-L. [1 ]
机构：
[1] Shougang Group Company Limited Research Institute of Technology, Beijing
来源：
Surface Technology | 2021年 / 50卷 / 08期
关键词：
Al-Si coating; EBSD; Hot dip; Kikuchi pattern; Phase;
D O I：
10.16490/j.cnki.issn.1001-3660.2021.08.037
中图分类号：
学科分类号：
摘要：
This paper aims to study the microstructure and phase composition of hot-dip Al-Si coating on hot-formed steel. Scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDS) were used to analyze the microstructure and composition of the surface and cross-section of the Al-Si coating, X-ray diffraction (XRD) and electron backscatter diffraction (EBSD) were used to analyze the phase composition and ratio of the Al-Si coating. The surface of the hot-dip Al-Si coating is composed of Al-rich phase, a small amount of Fe-rich phase, and high Si phase with dendritic network distribution, the cross-section of the hot-dip Al-Si coating is composed of inner and outer layers, the inner layer close to the iron matrix is an Fe-Al-Si alloy layer, and the outer layer is an Al-Si layer. Further research shows that the Al-Si layer is composed of Al-rich phase, a small amount of Fe-rich phase, and columnar distributed high Si phase, the high Si phase mainly exists at the interface between the alloy layer and the Al-Si layer and in the Al-Si layer. The phases of Al-rich phase, Fe-rich phase, high Si phase and Fe-Al-Si ternary alloy layer in the hot-dip Al-Si coating are Al, Al13Fe4, Si and Al8Fe2Si respectively. The study of high Si phase in hot-dip Al-Si coating has shown that the high-Si phase distributed at the interface between the alloy layer and the Al-Si layer can effectively hinder the growth of the coating, while the high-Si phase distributed in the Al-Si layer exists in the form of a three-dimensional network framework in space. This three-dimensional network structure as the main frame of the coating can effectively improve the strength and toughness and formability of the coating. © 2021, Chongqing Wujiu Periodicals Press. All rights reserved.
引用
收藏
页码：375 / 381
页数：6
相关论文
共 25 条
  • [1] Yan-Hong M.U., Bao-Yu W.A.N.G., Jing Z., Et al., Influences of hot stamping parameters on mechanical properties and microstructure of 30MnB5 and 22MnB5 quenched in flat die[J], Journal of Central South University, 25, 4, pp. 736-746, (2018)
  • [2] Hong-Lin Y., Shen-Gen Z.H., Ji-Yao H., Et al., Development research on 22MnB5 hot stamping steel[J], Forging & Stamping Technology, 39, 1, pp. 1-5, (2014)
  • [3] Jun-Ye C., Ai-Min Z.H.A.O., Yin-Li C., Et al., Efect of tempering temperature on the microstructure and mechanical properties of 30MnB5 hot stamping steel after quenching[J], Journal of University of Science and Technology Beijing, 35, 9, pp. 1150-1157, (2013)
  • [4] Kai-Xiang G., Wu-Rong W.A.N.G., Xi-Cheng W., Et al., High-temperature friction of uncoated 22MnB5 boron steel in hot stamping[J], Journal of Shanghai Jiao Tong University, 53, 9, pp. 1136-1142, (2019)
  • [5] Nikravesh M., Naderi M., Akbari G.H., Influence of hot plastic deformation and cooling rate on martensite and bainite start temperatures in 22MnB5 steel[J], Materials Science and Engineering: A, 540, pp. 24-29, (2012)
  • [6] Yong L.I., Jia-Dong L.I., Tian-Liang F.U., Et al., New heating technology of hot stamping[J], Heat Treatment of Metals, 39, 7, pp. 66-71, (2014)
  • [7] Yuan Z., Qi L.I., Sha-Sha J.I., Et al., Research on preparing process and oxidation resistance of aluminum silicon coating for 22MnB5 hot forming steel[J], Hot Working Technology, 48, 8, pp. 145-148, (2019)
  • [8] Wang C.J., Chen S.M., The high-temperature oxidation behavior of hot-dipping Al-Si coating on low carbon steel[J], Surface and Coatings Technology, 200, 22-23, pp. 6601-6605, (2006)
  • [9] Zandrahimi M., Vatandoost J., Ebrahimifar H., Al, Si, and Al-Si coatings to improve the high-temperature oxidation resistance of AISI 304 stainless steel[J], Oxidation of Metals, 76, 3-4, pp. 347-358, (2011)
  • [10] Li-Ping C., Li L.I., Shi-Wei Y., Et al., Effect of silicon on resistant high temperature oxidation of Ni-based superalloy with Al-Si coating[J], Research on Metallic Materials, 3, pp. 36-39, (2004)
123