Preparation of a self-matting, anti-fingerprint and skin-tactile wood coating via biomimetic self-wrinkling patterns

Inspired by natural wrinkled surfaces, artificial surfaces with biomimetic wrinkled structures have been widely used to improve optical properties, wettability, and antibacterial properties. However, the preparation of wrinkled structures has the disadvantages of long-time consumption and complex processes. Herein, we prepared a self-wrinkling polyurethane-acrylate (PUA) wood coating via biomimetic self-wrinkling patterns by using a light-emitting diode (LED)/excimer/mercury lamp curing system, which was capable of self-matting, anti-fingerprint and skin-tactile performance. By adjusting the irradiation intensity in the curing system, the wavelength (lambda) and amplitude (A) of wrinkles on the coating surface were controlled to enhance the coating performance. After curing by the LED, excimer, and mercury lamps at energy intensities of 500, 30, and 300 mW/cm2 respectively, the self-wrinkling coating showed excellent surface performance. The self-wrinkling coating represented low gloss of 4.1 GU at 85 degrees, high hardness of 4H. Interestingly, the coating surface had a high hydrophobicity (104.5 degrees) and low surface energy (29-30 mN/m) and low coefficient (COF) of friction (0.1-0.2), which were consistent with those of the human skin surface. Besides, the wrinkled structure also improved the thermal stability of the coating samples. This study provided a promising technique for the mass production of self-wrinkling coatings that could be used in wood-based panels, furniture, and leather.