Defect Repair and Ablation Resistance of the Damaged SiC-ZrB2 Coating for C / C Composites

被引：0
|
作者：
Wang W. [1 ]
Fu Q. [1 ]
Hu D. [1 ]
Xie W. [1 ]
Liu T. [1 ]
机构：
[1] Shaanxi Province C / C Composites Technology Research Center, Northwestern Polytechnical University, Xi’an
来源：
Zhongguo Biaomian Gongcheng/China Surface Engineering | 2022年 / 35卷 / 06期
基金：
中国国家自然科学基金;
关键词：
ablation resistance; C / C composites; defect repair; SiC-ZrB[!sub]2[!/sub] coating;
D O I：
10.11933/j.issn.1007-9289.20220218003
中图分类号：
学科分类号：
摘要：
Defects such as cracks, pits and holes, appear in the coatings of carbon / carbon (C / C) composite materials during the preparation and service process, which make coatings lose their integrity and lead to protection failure. Replacing the integral coating as a commonly used solution is expensive, complicated and time-consuming. Therefore, a fast and efficient repairing technology for minor defects on coatings is an effective way to solve this problem. Defects are pre-fabricated on the surface of SiC-ZrB2 (SZ) coated C / C composites by supersonic atmospheric plasma flame. To repair the defects of the SZ coating, isopropanol and boron-containing polynitrosilane adhesive with stable performance at high temperatures are used as repairing agents. SiC-ZrB2 and Al2O3 are used as modified filler and sintering aid, respectively. The microstructure and ablation resistance of the coating before and after repair are studied. The results show that circular pit defects appear in the center of the coating sample after plasma flame ablation, exposing the C / C composite substrate. For the coating sample after repair, SiBCN ceramics and modified ceramic fillers generated by the pyrolysis of the repair agent cover the defects evenly, and thus the coating sample maintains high integrity. A dense SiO2 glass film can be formed under oxyacetylene ablation, which effectively blocks oxygen diffusion and protect C / C composites from mechanical erosion. The repaired coating sample shows a better ablation resistance under oxyacetylene flame flow. After ablated for 60 s, its line ablation rate and mass ablation rate are 0.65 μm / s and -0.28 mg / s, respectively, which decrease by 83.54% and 129.47% compared with the unrepaired coating samples, suggesting that the ablation resistance of the repaired coating is significantly improved. © 2022 Chinese Mechanical Engineering Society. All rights reserved.
引用
收藏
页码：214 / 221
页数：7
相关论文
共 29 条
  • [1] FU Q G, ZHANG P, ZHUANG L, Et al., Micro / nano multiscale reinforcing strategies toward extreme high-temperature applications: Take carbon / carbon composites and their coatings as the examples, Journal of Materials Science & Technology, 96, pp. 31-68, (2022)
  • [2] TIAN S, ZHOU L, LIANG Z, Et al., 2.5 D carbon / carbon composites modified by in situ grown hafnium carbide nanowires for enhanced electromagnetic shielding properties and oxidation resistance, Carbon, 161, pp. 331-340, (2020)
  • [3] FU Q G, ZHUANG L, REN Q W, Et al., Carbon nanotube-toughened interlocking buffer layer to improve the adhesion strength and thermal shock resistance of SiC coating for C / C-ZrC-SiC composites, Journal of Materiomics, 1, 3, pp. 245-252, (2015)
  • [4] LIU X, DENG H L, ZHENG J H, Et al., Mechanical and thermal conduction properties of carbon / carbon composites with different carbon matrix microstructures, New Carbon Materials, 35, 5, pp. 576-584, (2020)
  • [5] LIU Lantao, CHEN Guanyu, YI Liming, Et al., Study on the ablation mechanism of C / C composite throat for solid rocket motor, Carbon Technology, 40, 3, pp. 31-35, (2021)
  • [6] WANG W Y, FU Q G, TAN B Y., Effect of in-situ grown SiC nanowires on the mechanical properties of HfC-ZrB<sub>2</sub>-SiC modified C / C composites, Journal of Alloys and Compounds, 726, pp. 866-874, (2017)
  • [7] WANG L, WANG W Y, FU Q G., The improvement of the self-healing ability of MoSi<sub>2</sub> coatings at 900 ~ 1 200 ºC by introducing SiB<sub>6</sub>, Journal of the European Ceramic Society, 40, 8, pp. 2896-2906, (2020)
  • [8] PENG Xuefeng, DAI Zongmiao, JIANG Jianjun, Et al., Nanoindentation behavior of C / C composites with the different carbon matrices, Equipment and Environmental Engineering, 10, pp. 64-70, (2019)
  • [9] FU Y Q, ZHANG Y L, ZHANG J, Et al., Mechanical properties and ablation resistance of HfC nanowire modified carbon / carbon composites, Ceramics International, 46, 10, pp. 16142-16150, (2020)
  • [10] FENG G H, LI H J, YAO X Y, Et al., Ablation resistance of TaC-modified HfC coating prepared by supersonic plasma spraying for SiC-coated carbon / carbon composites, Ceramics International, 45, 14, pp. 17936-17945, (2019)
123