Thermal degradation, flame retardancy and mechanical properties of DOPO derivatives/poly(lactic acid) composites

被引：0
|
作者：
Xu W. [1 ,2 ]
Long L. [2 ]
Xu G. [1 ,2 ]
Huang S. [2 ]
Xiang Y. [2 ]
Li J. [2 ]
Qin S. [2 ]
He M. [1 ]
Yu J. [1 ,2 ]
机构：
[1] College of Materials and Metallurgy, Guizhou University, Guiyang
[2] National Engineering Research Center for Compounding and Modification of Polymer Materials, Guiyang
来源：
Fuhe Cailiao Xuebao/Acta Materiae Compositae Sinica | 2021年 / 38卷 / 09期
关键词：
DOPO derivatives; Flame retardancy; Mechanical properties; PLA; Thermal degradation;
D O I：
10.13801/j.cnki.fhclxb.20201124.003
中图分类号：
学科分类号：
摘要：
The thermal decomposition behaviors of three kinds of derivatives, including 9, 10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide(DOPO), 10-(2, 5-dihydroxyphenyl)-10-hydro-9-oxa-10-phosphaphenanthrene-10-oxide(DOPO-HQ), 6H-dibenz[c, e][1, 2]oxaphosphorin, 6'6-(1, 2-phenethyl)bis-, 6'6-dioxide (DiDOPO), were studied. And effects of these DOPO derivatives on the thermal degradation behavior, flame retardancy and mechanical properties of poly(lactic acid) (PLA) were comparatively studied. TG results show that the initial decomposition temperature (T5%) of DOPO is 154℃, and an increased T5% of DOPO-HQ of 342℃ is displayed. In addition, T5% of DiDOPO reaches to as high as 363℃, which is higher than that of DOPO and DOPO-HQ. As for PLA composites, T5% reveals an increase trend as follow: T5%(DOPO/PLA, 273.5℃) < T5%(DOPO-HQ/PLA, 321.5℃) < T5%(DiDOPO/PLA, 333.8℃). T5% shows an progressively increase trend with the increased thermal stability of flame retardants. Furthermore, the thermal degradation kinetics results indicate that the thermal degradation activation energy of the composites material is improved. The thermal degradation of DOPO derivatives/PLA composites was investigated by thermogravimetric-infrared spectroscopy analysis (TG-IR) and pyrolysis-gas chromatography/mass spectrometry (PY-GC/MS). It shows that the three flame retardants mainly exert their gas phase flame retardant effect by generating phosphorus oxygen free radicals, and the characteristic groups of DOPO-HQ and DiDOPO may play a role in the condensation phase. All the three systems have attained the V-0 rating (UL-94), what's more DOPO/PLA dripping is the most serious, on the contrary the dripping of DiDOPO/PLA is suppressed. Furthermore, the mechanical test results indicate that the tensile strength of DOPO/PLA decreases by 83.1% compared with pure PLA, while DOPO-HQ/PLA and DiDOPO/PLA only drops by 14.2% and 15.6%, respectively. © 2021, Editorial Office of Acta Materiae Compositae Sinica. All right reserved.
引用
收藏
页码：2841 / 2854
页数：13
相关论文
共 29 条
  • [1] ZHOU X, YANG R, WANG B, Et al., Development and characterization of bilayer films based on pea starch/polylactic acid and use in the cherry tomatoes packaging, Carbohydrate Polymers, 222, (2019)
  • [2] ASHWIN B, ABINAYA B, PRASITH T P, Et al., 3D-poly (lactic acid) scaffolds coated with gelatin and mucic acid for bone tissue engineering, International Journal of Biological Macromolecules, 162, pp. 523-532, (2020)
  • [3] JEOUNG S K, HA J U, KO Y K, Et al., Aerobic biodegradability of polyester/polylactic acid composites for automotive NVH parts, International Journal of Precision Engineering and Manufacturing, 15, 8, pp. 1703-1707, (2014)
  • [4] WANG Xianpeng, LIU Yang, WANG Chuandong, Et al., Preparation of small-diameter collagen-polylactic acid artificial blood vessel by electrospinning, Acta Materiae Compositae Sinica, 34, 11, pp. 2550-2555, (2017)
  • [5] CHEN Yajun, MAO Xiaojun, WANG Chao, Et al., Research Progress in Flame Retardant of Poly (lactic acid), China Plastics, 29, 3, pp. 1-8, (2015)
  • [6] JIANG P, GU X, ZHANG S, Et al., Synthesis, characterization, and utilization of a novel phosphorus/nitrogen-containing flame retardant, Industrial & Engineering Chemistry Research, 54, 11, pp. 2974-2982, (2015)
  • [7] XI W, QIAN L, QIU Y, Et al., Flame-retardant behavior of Bi-group molecule derived from phosphaphenanthrene and triazine groups on polylactic acid, Polymers for Advanced Technologies, 27, 6, pp. 781-788, (2016)
  • [8] CAO Y, WANG X, ZHANG W, Et al., Bi-DOPO structure flame retardants with or without reactive group: Their effects on thermal stability and flammability of unsaturated polyester, Industrial & Engineering Chemistry Research, 56, 20, pp. 5913-5924, (2017)
  • [9] HUDSON R F., The nature of the chemical bonding in organo-phosphorus compounds, Pure & Applied Chemistry, 9, 2, pp. 371-386, (1964)
  • [10] WENDELS S, CHAVEZ T, BONNET M, Et al., Recent developments in organophosphorus flame retardants containing P—C bond and their applications, Materials, 10, 7, (2017)
123