Enhancement of the interlaminar performance of silica/phenolic laminates after high-temperature pyrolysis using a boron carbide/silicon carbide fibre z-pin

被引：0
|
作者：
Fu, Huadong [1 ,2 ]
Qin, Yan [1 ,2 ]
Zou, Zhenyue [1 ,2 ]
Fan, Jiamin [1 ,2 ]
Xue, Chenyi [1 ,2 ]
机构：
[1] School of Materials Science and Engineering, Wuhan University of Technology, Wuhan,430070, China
[2] Key Laboratory of Special Materials Technology, Wuhan University of Technology, Wuhan,430070, China
来源：
Materials and Design | 2022年 / 219卷
关键词：
All Open Access; Gold;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
43
引用
收藏
相关论文
共 5 条
  • [1] Enhancement of the interlaminar performance of silica/phenolic laminates after high-temperature pyrolysis using a boron carbide/silicon carbide fibre z-pin
    Fu, Huadong
    Qin, Yan
    Zou, Zhenyue
    Fan, Jiamin
    Xue, Chenyi
    MATERIALS & DESIGN, 2022, 219
  • [2] Time-dependent high-temperature compressive failure behavior of high-silica/boron-phenolic composites modified with boron carbide and talc
    Wang, Huanfang
    Dong, Chuang
    Hu, Wei
    Dang, Haoyuan
    Du, Chunlin
    Ou, Yun
    Shi, Minxian
    Zhang, Chao
    COMPOSITES SCIENCE AND TECHNOLOGY, 2022, 221
  • [3] Enhancement of the Mechanical Performance of SiCf/Phenolic Composites after High-temperature Pyrolysis Using ZrC/B4C Particles
    Ding, Jie
    Li, Yan
    Shi, Minxian
    Huang, Zhixiong
    Qin, Yan
    Zhuang, Yingluo
    Wang, Cunku
    JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2023, 38 (06): : 1262 - 1268
  • [4] Enhancement of the Mechanical Performance of SiCf/Phenolic Composites after High-temperature Pyrolysis Using ZrC/B4C Particles
    Jie Ding
    Yan Li
    Minxian Shi
    Zhixiong Huang
    Yan Qin
    Yingluo Zhuang
    Cunku Wang
    Journal of Wuhan University of Technology-Mater. Sci. Ed., 2023, 38 : 1262 - 1268
  • [5] Enhancement of the Mechanical Performance of SiCf/Phenolic Composites after High-temperature Pyrolysis Using ZrC/B4C Particles
    丁杰
    LI Yan
    石敏先
    HUANG Zhixiong
    QIN Yan
    ZHUANG Yingluo
    WANG Cunku
    JournalofWuhanUniversityofTechnology(MaterialsScience), 2023, 38 (06) : 1262 - 1268
1